Glass substrate for flat panel display

ABSTRACT

A flat panel display glass substrate includes a glass comprising, in mol %, 55-80% SiO 2 , 3-20% Al 2 O 3 , 3-15% B 2 O 3 , and 3-25% RO (the total amount of MgO, CaO, SrO, and BaO). The contents in mol % of SiO 2 , Al 2 O 3 , and B 2 O 3  satisfy a relationship (SiO 2 +Al 2 O 3 )/(B 2 O 3 )=7.5-17. The strain point of the glass is 665° C. or more. The devitrification temperature of the glass is 1250° C. or less. The substrate has a heat shrinkage rate of 75 ppm or less. The rate of heat shrinkage is calculated from the amount of shrinkage of the substrate measured after a heat treatment which is performed at a rising and falling temperature rate of 10° C./min and at 550° C. for 2 hours by the rate of heat shrinkage (ppm)={the amount of shrinkage of the substrate after the heat treatment/the length of the substrate before the heat treatment}×10 6 .

This application is a Divisional of U.S. application Ser. No. 13/537,615, filed Jun. 29, 2012, which claims priority to Provisional U.S. Application No. 61/513,205 filed Jul. 29, 2011; which claims priority to Japanese Application No. 2011-147758, filed Jul. 1, 2011 and JP 2012-059132 filed Mar. 15, 2012, the disclosure of each is incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to glass substrates for flat panel displays and methods for manufacturing the glass substrates.

2. Related Background Art

Flat panel displays with small thickness and low power consumption, such as a thin film transistor (TFT) liquid crystal display and an organic electroluminescence (EL) display, have in recent years been employed as displays for mobile devices and the like. These displays typically include a glass substrate.

There are the following types of TFTs: an amorphous silicon (α-Si) TFT; and a polysilicon (p-Si) TFT. The p-Si TFT is advantageous over the α-Si TFT in terms of screen resolution, display durability, display thickness and weight, and power consumption, and the like, i.e., the p-Si TFT can provide a beautiful screen with a higher resolution, a display with a higher durability, a display with a smaller thickness and a lower weight, and lower power consumption. Conventionally, however, a high temperature treatment is required in production of the p-Si TFT. Therefore, the glass substrate undergoes heat shrinkage and heat shock during production of the p-Si TFT, and therefore, glass other than silica glass cannot be employed. As a result, it is difficult to apply the p-Si TFT to a liquid crystal display.

However, the low-temperature polysilicon (LTPS) TFT, for which the heat treatment is performed at lower temperature, has in recent years been developed, and therefore, the p-Si TFT has been applicable to the flat panel display. As a result, the display of a small device (e.g., a mobile device, etc.) can have a beautiful screen with a high resolution.

Note that the heat treatment in production of the p-Si TFT still requires a temperature of as high as 400 to 600° C. Most of the conventional glass substrates for displays do not have a sufficiently high strain point, and therefore, are likely to undergo significant heat shrinkage due to the heat treatment in production of the p-Si TFT, leading to a non-uniform pixel pitch. Moreover, in recent years, there has been a demand for higher and higher resolutions. Therefore, in order to reduce such a non-uniform pixel pitch, it is highly desirable to reduce the heat shrinkage of the glass substrate during production of the display. Conventionally, glass substrates for displays which have been developed in view of the heat shrinkage problem have been reported (JP 2002-3240A, JP 2004-315354A, and JP 2007-302550A).

SUMMARY OF THE INVENTION

Here, the heat shrinkage of the glass substrate can be reduced by increasing characteristic (low-temperature viscosity characteristic) temperatures in the low temperature viscosity range, typified by a glass transition temperature (hereinafter referred to as a “Tg”) and a strain point (the “Tg and strain point” will be described hereinafter as typical examples of the low-temperature viscosity characteristic temperature in this specification). However, if the composition of a glass is modified only for the purpose of increasing the Tg and strain point of the glass, the devitrification resistance of the glass is likely to deteriorate. If the devitrification resistance deteriorates, i.e., the devitrification temperature increases, so that the liquidus viscosity decreases, the flexibility of the production method also decreases. If the devitrification temperature increases, so that the liquidus viscosity decreases, it is difficult to produce the glass substrate, for example, by the overflow downdraw process.

Therefore, it is an object of the present invention to provide a glass substrate for flat panel displays which simultaneously has a high Tg and strain point and good devitrification resistance and in which a non-uniform pixel pitch does not occur even if the glass substrate is used in a display to which the p-Si TFT is applied.

A first example flat panel display glass substrate on which a p-Si TFT can be formed according to the present invention includes a glass comprising, as expressed in mol %:

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass, the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17,

the strain point of the glass is 665° C. or more, and

the devitrification temperature of the glass is 1250° C. or less, and

the glass substrate has a heat shrinkage rate of 75 ppm or less.

The ratio of heat shrinkage is calculated from the amount of shrinkage of the glass substrate measured after a heat treatment which is performed at a rising and falling temperature rate of 10° C./min and at 550° C. for 2 hours by:

the ratio of heat shrinkage (ppm)={the amount of shrinkage of the glass substrate after the heat treatment/the length of the glass substrate before the heat treatment}×10⁶

The “ratio of heat shrinkage” as used hereinafter has the same meaning.

A second example flat panel display glass substrate on which a p-Si TFT can be formed according to the present invention includes a glass comprising, as expressed in mol %;

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0, and

the devitrification temperature of the glass is 1250° C. or less, and

the glass substrate has a heat shrinkage rate of 60 ppm or less.

According to a third aspect of the present invention, a flat panel display glass substrate on which a p-Si TFT can be formed includes a glass comprising, as expressed in mol %;

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17,

the strain point of the glass is 665° C. or more, and

the devitrification temperature of the glass is 1250° C. or less, and

the glass substrate has a heat shrinkage rate of 75 ppm or less after a heat treatment in which the glass substrate is kept at Tg for 30 min, then cooled at a rate of 100° C./min until the temperature thereof reaches Tg−100° C., then cooled until the temperature reaches room temperature, and then kept at 550° C. for 2 hours, wherein a rising and falling temperature rate is 10° C./min.

A first example method for manufacturing a flat panel display glass substrate on which a p-Si TFT can be formed according to the present invention, includes:

a melting step of melting a glass material for a glass comprising, as expressed in mol %, 55-80% SiO₂, 3-20% Al₂O₃, 3-15% B₂O₃, and 3-25% RO (the total amount of MgO, CaO, SrO, and BaO), with the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfying a relationship (SiO₂+Al₂O₃)(B₂O₃)=7.5-17, the strain point of the glass being 665° C. or more, and the devitrification temperature of the glass being 1250° C. or less, to produce a molten glass;

a forming step of forming the molten glass into a glass plate; and

an annealing step of annealing the glass plate,

where

the glass plate has a heat shrinkage rate of 75 ppm or less.

A second example method for manufacturing a flat panel display glass substrate on which a p-Si TFT can be formed according to the present invention, includes:

a melting step of melting a glass material for a glass comprising, as expressed in mol %, 55-80% SiO₂, 3-20% Al₂O₃, 3-15% B₂O₃, and 3-25% RO (the total amount of MgO, CaO, SrO, and BaO), with the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfying a relationship (SiO₂+Al₂O₃)(B₂O₃)=8.45-17.0 and the devitrification temperature of the glass being 1250° C. or less, to produce a molten glass,

a forming step of forming the molten glass into a glass plate, and

an annealing step of annealing the glass plate,

wherein

the glass plate has a heat shrinkage rate of 60 ppm or less.

A first example flat panel display glass substrate according to the present invention includes a glass comprising, as expressed in mol %;

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17,

the strain point of the glass is 665° C. or more, and

the devitrification temperature of the glass is 1250° C. or less, and

the glass substrate has a heat shrinkage rate of 75 ppm or less.

A second flat panel display glass substrate according to the present invention includes a glass comprising, as expressed in mol %;

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0, and

the devitrification temperature of the glass is 1250° C. or less, and

the glass substrate has a heat shrinkage rate of 60 ppm or less.

The glass substrate of the present invention can simultaneously have both a high Tg and strain point and good devitrification resistance. Therefore, according to the present invention, a glass substrate having excellent properties can be provided in which the heat shrinkage caused by a heat treatment during production of a display is reduced, and therefore, the non-uniformity of the pixel pitch does not occur.

DETAILED DESCRIPTION OF THE INVENTION

A display glass substrate according to this embodiment includes a glass which comprises, as expressed in mol %, 55-80% SiO₂, 3-20% Al₂O₃, 3-15% B₂O₃, and 3-25% RO (the total amount of MgO, CaO, SrO, and BaO), where the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17. Another display glass substrate of this embodiment includes a glass which comprises, as expressed in mol %, 55-80% SiO₂, 3-20% Al₂O₃, 3-15% B₂O₃, and 3-25% RO (the total amount of MgO, CaO, SrO, and BaO), where the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0. If the relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17, more preferably the relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0, is satisfied, the glass substrate of this embodiment can have an increased Tg and strain point while maintaining good devitrification resistance. By the increase of the Tg and strain point, the amount of heat shrinkage occurring in a heat treatment during production of a display is reduced. If the amounts of SiO₂ and Al₂O₃ are simply increased and the amount of B₂O₃ is simply decreased in order to increase the Tg and strain point, the melting temperature may increase, i.e., the meltability may decrease. However, if SiO₂, Al₂O₃, and B₂O₃ satisfy the above relationship, the decrease of the meltability can be reduced. In other words, the glass substrate of this embodiment can have an increased Tg and strain point while maintaining good devitrification resistance and good meltability.

The glass included in the glass substrate of this embodiment may comprise 5% or less ZnO as an optional component. In this case, it is preferable that the contents in mol % of SiO₂ and Al₂O₃ satisfy SiO₂+Al₂O₃≧70%, more preferably SiO₂+Al₂O₃≧75%, and the contents in mol % of RO, ZnO, and B₂O₃ satisfy RO+ZnO+B₂O₃=7-25%.

The glass included in the glass substrate of this embodiment may have a strain point of 660° C. or more. In order to more reliably reduce the heat shrinkage during production of a flat panel display, the strain point is preferably 665° C. or more, more preferably 675° C. or more, even more preferably 680° C. or more, still even more preferably 685° C. or more, still even more preferably 690° C. or more, still even more preferably 695° C. or more, and still even more preferably 700° C. or more.

The meltability of a glass may be evaluated by glass temperature (melting temperature), where the viscosity is 10^(2.5) dPa·s. The glass included in the glass substrate of this embodiment preferably has a melting temperature of 1680° C. or less. If the melting temperature is 1680° C. or less, the glass substrate of this embodiment can have good meltability. If the melting temperature is excessively low, the Tg and strain point are likely to be low. Therefore, in order to achieve a high Tg and strain point, the melting temperature needs to be fairly high. Therefore, the melting temperature is preferably 1550-1650° C., more preferably 1550-1645° C., even more preferably 1580-1640° C., still even more preferably 1590-1630° C., and still even more preferably 1600-1620° C.

The amount of heat shrinkage may be reduced by appropriately adjusting conditions under which a glass is produced in addition to the aforementioned adjustment of a glass composition. Specifically, when the glass is annealed, then if the glass is cooled at a necessarily and sufficiently low rate in a temperature region of Tg to Tg−100° C., the amount of heat shrinkage can be reduced. Therefore, in the glass substrate of this embodiment, by optionally adjusting the conditions for the annealing as appropriate in addition to the aforementioned adjustment of a composition, the ratio of heat shrinkage can be caused to be 75 ppm or less, preferably 65 ppm or less, and more preferably 60 ppm or less. If the ratio of heat shrinkage is 75 ppm or less, preferably 65 ppm or less, and more preferably 60 ppm or less, even when the glass substrate of this embodiment is employed in a display to which the p-Si TFT is applied, and moreover, the display has a high resolution, the non-uniformity of the pixel pitch can be sufficiently reduced. In order to reliably reduce the non-uniformity of the pixel pitch, the ratio of heat shrinkage is preferably 55 ppm or less, more preferably 50 ppm or less, even more preferably 45 ppm or less, still even more preferably 43 ppm or less, still even more preferably 40 ppm or less, and still even more preferably 38 ppm or less. In other words, the ratio of heat shrinkage is 0-75 ppm, preferably 0-65 ppm, more preferably 0-60 ppm, even more preferably 0-55 ppm, still even more preferably 0-50 ppm, still even more preferably 0-45 ppm, still even more preferably 0-43 ppm, still even more preferably 0-40 ppm, and still even more preferably 0-38 ppm. Note that, in order to cause the ratio of heat shrinkage to be zero ppm, it may be necessary to perform the annealing for a considerably long time or perform a heat shrinkage reduction treatment (off-line annealing) after the annealing, leading to a reduction in productivity and an increase in cost. In view of productivity and cost, the ratio of heat shrinkage is, for example, 3-75 ppm, preferably 5-75 ppm, more preferably 5-65 ppm, even more preferably 8-55 ppm, still even more preferably 8-50 ppm, still even more preferably 10-45 ppm, still even more preferably 10-43 ppm, still even more preferably 10-40 ppm, and still even more preferably 15-38 ppm.

The glass included in the glass substrate of this embodiment has a devitrification temperature of 1250° C. or less. If the devitrification temperature is 1250° C. or less, the glass included in the glass substrate of this embodiment can be advantageously easily formed by a downdraw process. As a result, the surface quality of the glass substrate can be improved, and the manufacturing cost of the glass substrate can be reduced. If the devitrification temperature is excessively high, devitrification is likely to occur, i.e., the devitrification resistance decreases. Therefore, the devitrification temperature of the glass substrate of this embodiment preferably 1230° C. or less, more preferably 1220° C. or less, even more preferably 1210° C. or less, and still even more preferably 1200° C. or less. On the other hand, in order to achieve properties of a substrate for flat panel displays, such as low heat shrinkage and low density, the devitrification temperature of the glass included in the glass substrate is preferably 1050-1250° C., more preferably 1110-1250° C., even more preferably 1150-1240° C., still even more preferably 1160-1230° C., and still even more preferably 1170-1220° C.

The glass included in the glass substrate of this embodiment preferably has a liquidus viscosity of 10^(4.0) dPa·s or more, more preferably 10⁴⁵ dPa·s or more. If the liquidus viscosity is 10^(4.0) dPa·s or more, the glass can be easily formed by a float process. If the liquidus viscosity is 10⁴⁵ dPa·s or more, the ease of forming is further improved. Therefore, if the liquidus viscosity is within such a range, the glass included in the glass substrate of this embodiment can be easily formed by a downdraw process (particularly, the overflow downdraw process). As a result, the surface quality of the glass substrate can be improved and the manufacturing cost of the glass substrate can be reduced. The liquidus viscosity is more preferably 10^(4.5)-10^(6.0) dPa·s, more preferably 10^(4.5)-10^(5.9) dPa·s, even more preferably 10^(4.6)-10^(5.8) dPa·s, still even more preferably 10^(4.6)-10^(5.7) dPa·s, still even more preferably 10^(4.7)-10^(5.7) dPa·s, still even more preferably 10^(4.8)-10^(5.6) dPa·s, and still even more preferably 10^(4.9)-10^(5.5) dPa·s.

Other properties of the glass included in the glass substrate of this embodiment are preferably within the following ranges.

The average coefficient of thermal expansion within the range of 100-300° C. of the glass included in the glass substrate of this embodiment is preferably less than 37×10⁻⁷K⁻¹, more preferably no less than 28×10⁻⁷K⁻¹ and less than 36×10⁻⁷K⁻¹, even more preferably no less than 30×10⁻⁷K⁻¹ and less than 35×10⁻⁷K⁻¹, still even more preferably no less than 31×10⁻⁷K⁻¹ and less than 34.5×10⁻⁷K⁻¹, and still even more preferably no less than 32×10⁻⁷K⁻¹ and less than 34×10⁻⁷K⁻¹. If the coefficient of thermal expansion is excessively high, the heat shock or the amount of heat shrinkage increases in the heat treatment during production of a display. On the other hand, if the coefficient of thermal expansion is excessively low, it is difficult to match the coefficients of thermal expansion of peripheral materials, such as a metal and an organic adhesive, formed on the glass substrate during production of a display, and therefore, the peripheral materials are likely to come off the glass substrate. In the p-Si TFT production process, rapid heating and rapid cooling are repeatedly performed, and therefore, greater heat shock is applied to the glass substrate. When the glass substrate is large, a temperature difference (temperature distribution) is likely to occur in the heat treatment step, leading to an increase in the probability of destruction of the glass substrate. If the coefficient of thermal expansion is within the aforementioned range, thermal stress caused by a difference in thermal expansion can be reduced, resulting in a decrease in the probability of destruction of the glass substrate in the heat treatment step. Note that when importance is put on the matching with the coefficients of thermal expansion of the peripheral materials, such as a metal and an organic adhesive, formed on the glass substrate, the average coefficient of thermal expansion within the range of 100-300° C. of the glass included in the glass substrate is preferably less than 55×10⁻⁷K⁻¹, more preferably less than 40×10⁻⁷K⁻¹, even more preferably no less than 28×10⁻⁷K⁻¹ and less than 40×10⁻⁷K⁻¹, still even more preferably no less than 30×10⁻⁷K⁻¹ and less than 39×10⁻⁷K⁻¹, still even more preferably no less than 32×10⁻⁷K⁻¹ and less than 38×10⁻⁷K⁻¹, and still even more preferably no less than 34×10⁻⁷K⁻¹ and less than 38×10⁻⁷K⁻¹.

If the Tg is excessively low, the heat resistance decreases, and in the heat treatment step, the heat shrinkage increases. Therefore, the Tg of the glass substrate of this embodiment is preferably 720° C. or more, more preferably 740° C. or more, even more preferably 745° C. or more, still even more preferably 750° C. or more, still even more preferably 755° C. or more, and still even more preferably 760° C. or more.

If the density is excessively high, it may be difficult to reduce the weight of the glass substrate, and therefore, it may be difficult to reduce the weight of a display. Therefore, the density of the glass substrate of this embodiment is preferably 2.6 g/cm³ or less, more preferably less than 2.5 g/cm³, even more preferably 2.45 g/cm³ or less, still even more preferably 2.42 g/cm³ or less, and still even more preferably 2.4 g/cm³ or less. In particular, in order to reduce the weight of the glass substrate for a flat display or an organic EL display including the p-Si TFT, the density is preferably less than 2.5 g/cm³, more preferably 2.45 g/cm³ or less, even more preferably 2.42 g/cm³ or less, and still even more preferably 2.4 g/cm³ or less.

If the specific resistance of a glass melt is excessively low, then when a glass material is electrically melted, the value of a current required for melting the glass material is excessively large. Therefore, there may be constraints on equipment. Moreover, the electrode is disadvantageously much consumed. On the other hand, if the specific resistance is excessively high, then when the glass material is melted, a current flows through heat-resistant bricks forming a melting bath, likely leading to damage to the melting bath. Therefore, the specific resistance at 1550° C. of the glass included in the glass substrate of this embodiment is preferably 50-300 Ω·cm, more preferably 50-250 Ω·cm, even more preferably 80-240 Ω·cm, and still even more preferably 100-230 Ω·cm.

If the Young's modulus and specific modulus of elasticity (Young's modulus/density) are excessively low, the glass substrate is bent or warped by its own weight during production of a display, likely leading to damage to the glass substrate. In particular, if the glass substrate is large (e.g., 2000 mm or more wide), the damage caused by the bending or warp becomes significant. Therefore, the Young's modulus of the glass substrate of this embodiment is preferably 70 GPa or more, more preferably 73 GPa or more, even more preferably 74 GPa or more, and still even more preferably 75 GPa or more. The specific modulus of elasticity of the glass substrate of this embodiment is preferably 28 GPa or more, more preferably 29 GPa or more, even more preferably 30 GPa or more, and still even more preferably 31 GPa or more.

Next, components of the glass included in the glass substrate of this embodiment will be described. Note that “mol %” is simply hereinafter shortened to “%”.

(SiO₂)

SiO₂ is a skeltal and essential component. If the amount of SiO₂ is excessively small, the acid resistance may decrease, the Tg and strain point may decrease, the coefficient of thermal expansion may increase, and the buffered hydrofluoric acid (BHF) resistance may decrease. It may also be difficult to reduce the density. On the other hand, if the amount of SiO₂ is excessively large, the melting temperature may be significantly high, and therefore, it may be difficult to melt and form the glass. The devitrification resistance may also decrease. Also, when the glass is slimmed down, the etching rate cannot be sufficiently increased. Therefore, the SiO₂ content is preferably 55-80%, more preferably 60-78%, even more preferably 62-78%, still even more preferably 65-78%, and still even more preferably 65-75%. Note that when the glass substrate comprises only less than 3% SrO+BaO in order to further reduce the weight, the SiO₂ content is more preferably 67-73%, even more preferably 69-72%. In order to sufficiently increase the etching rate when the glass is slimmed down, the SiO₂ content is more preferably 62-78%, even more preferably 62-73%, and still even more preferably 64-70%. On the other hand, when the glass substrate comprises 3% or more SrO+BaO, the SiO₂ content is more preferably 65-73%, even more preferably 66-71%.

(Al₂O₃)

Al₂O₃ is an essential component which reduces phase separating and increases the Tg and strain point. If the amount of Al₂O₃ is excessively small, the glass is likely to undergo phase separating. Also, the Tg and strain point may decrease, so that the heat resistance may decrease, the ratio of heat shrinkage may increase, and the Young's modulus may decrease. Also, the rate of etching the glass cannot be sufficiently increased. On the other hand, if the amount of Al₂O₃ is excessively large, the devitrification temperature of the glass increases, so that the devitrification resistance decreases, and therefore, the ease of forming deteriorates. Therefore, the Al₂O₃ content is preferably 3-20%, more preferably 5-18%, and even more preferably 5-15%. Note that when the glass substrate comprises only less than 3% SrO+BaO in order to further reduce the weight, the Al₂O₃ content is more preferably 7-13%, even more preferably 9-12%. In order to sufficiently increase the etching rate when the glass is slimmed down, the Al₂O₃ content is more preferably 7-15%, even more preferably 9-14%, and still even more preferably 10⁻¹⁴%. On the other hand, when the glass substrate comprises 3% or more SrO+BaO, the Al₂O₃ content is more preferably 8-15%, even more preferably 10-14%.

(B₂O₃)

B₂O₃ is an essential component which reduces the viscosity characteristic (high-temperature viscosity characteristic) temperature in a high temperature region, typified by the melting temperature, to improve the meltability (the “melting temperature” will be described hereinafter as a typical example of the “high-temperature viscosity characteristic temperature” in this specification). If the amount of B₂O₃ is excessively small, the meltability may decrease, the BHF resistance may decrease, the devitrification resistance may decrease, and the coefficient of thermal expansion may increase. Also, the density may increase, so that it may be difficult to reduce the density. On the other hand, if the amount of B₂O₃ is excessively large, the Tg and strain point may decrease, the acid resistance may decrease, and the Young's modulus may decrease. Also, B₂O₃ evaporates during melting of the glass, so that the non-uniformity of the glass may become significant, and therefore, a cord is likely to occur. Therefore, the B₂O₃ content is preferably 3-15%, more preferably 3-13%, and even more preferably 3-10%. Note that when the glass substrate comprises only less than 3% SrO+BaO in order to further reduce the weight, the B₂O₃ content is more preferably no less than 3% and less than 9.5%, even more preferably no less than 3.5% and less than 9.2%, still even more preferably no less than 4% and less than 8.9%, still even more preferably 5-8.5%, and still even more preferably 6-8%. Moreover, in order to prevent the increase of the devitrification temperature, the B₂O₃ content is more preferably 5-13%, even more preferably 5-12%, and still even more preferably 6% to less than 10% (no less than 6% and less than 10%). On the other hand, when the glass substrate comprises 3% or more SrO+BaO, the B₂O₃ content is more preferably 3-9%, even more preferably 4-8%.

(MgO)

MgO is a component which improves the meltability. MgO is also a component which hardly increases the density compared with other alkaline-earth metals. Therefore, if the MgO content is relatively increased, the density of the glass can be easily reduced. In the glass substrate of this embodiment, MgO is not essential. However, if MgO is comprised, the meltability can be increased and the occurrence of chips can be reduced. Therefore, MgO may be comprised. However, if the amount of MgO is excessively large, the Tg and strain point may decrease, the heat resistance may decrease, and the acid resistance may decrease. Also, the devitrffication temperature may increase, i.e., the devitrffication resistance may decrease, and therefore, it may be difficult to employ a downdraw process. Therefore, in the glass substrate of this embodiment, the MgO content is preferably 0-15%, more preferably 0-10%. Note that when the glass substrate comprises only less than 3% SrO+BaO in order to further reduce the weight, the MgO content is more preferably 0-5%, even more preferably 0% to less than 2% (no less than 0% and less than 2%), still even more preferably 0-1.5%, still even more preferably 0-1%, and still even more preferably 0-0.5%, and still even more preferably, substantially no MgO is comprised. Note that, as used herein, “substantially no MgO is comprised” means that MgO is not added as a material to the glass material, and the MgO content is preferably 0.2% or less, more preferably 0.15% or less, and even more preferably 0.1% or less. The phrase “substantially no X (X: a predetermined component) is comprised” has the same meaning. On the other hand, when the glass substrate comprises 3% or more SrO+BaO, the MgO content is more preferably 1-9%, even more preferably 2-8%.

(CaO)

CaO is a component which is effective in improving the meltability of a glass without rapidly increasing the devitrffication temperature of the glass. CaO is also a component which increases the density more slowly than other alkaline-earth metals. Therefore, if the CaO content is relatively increased, the density of the glass can be easily reduced. If the amount of CaO is excessively small, the meltability and devitrification resistance are likely to decrease due to an increase in the viscosity at high temperature. On the other hand, if the amount of CaO is excessively large, the coefficient of thermal expansion is likely to increase. For these reasons, the CaO content is preferably 0-20%, more preferably 0-18%. Note that when the glass substrate comprises only less than 3% SrO+BaO in order to further reduce the weight, the CgO content is more preferably 3.6-16%, even more preferably 4-16%, still even more preferably 6-16%, still even more preferably more than 7% and no more than 16%, still even more preferably 8-13%, and still even more preferably 9-12%. On the other hand, when the glass substrate comprises 3% or more SrO+BaO, the CaO content is more preferably 0-10%, even more preferably 0-5%, and still even more preferably 0-3%.

(SrO)

SrO is a component which can decrease the devitrification temperature of a glass. SrO is not an essential component, but if SrO is comprised, the devitrification resistance and meltability can be improved, and therefore, SrO may be comprised. However, if the amount of SrO is excessively large, the density increases. Therefore, if it is desirable that the density be reduced, preferably substantially no SrO is comprised. Therefore, in the glass substrate of this embodiment, the SrO content is preferably 0-10%, more preferably 0-8%. Note that, in order to further reduce the weight, the SrO content is preferably less than 3%, more preferably 2% or less, even more preferably 1% or less, and still even more preferably 0.5% or less, and still even more preferably, substantially no SrO is comprised. In other words, the SrO content is preferably 0% to less than 3% (no less than 0% and less than 3%), more preferably 0-2%, even more preferably 0-1%, and still even more preferably 0-0.5%, and still even more preferably, substantially no SrO is comprised. On the other hand, if it is desirable that the meltability be improved, the SrO content is more preferably 1-8%, even more preferably 3-8%.

(BaO)

BaO is a component which improves the devitrification resistance and meltability. Also, if BaO is comprised, the coefficient of thermal expansion increases and the density excessively increases. Therefore, in the glass substrate of this embodiment, the BaO content is preferably 0-10%, more preferably 0-5%, even more preferably 0-2%, and still even more preferably 0-1%. In view of the environmental load problem, more preferably substantially no BaO is comprised.

(Li₂O, Na₂O)

Li₂O and Na₂O are components which improve the meltability of a glass, but increases the coefficient of thermal expansion of the glass, leading to damage to a substrate in a heat treatment during production of a display, or significantly decreases the Tg and strain point of the glass, leading to an excessive decrease in the heat resistance. Therefore, in the glass substrate of this embodiment, the Li₂O and Na₂O content is preferably 0-0.3%, more preferably 0-0.2%, and even more preferably 0-0.1%, and still even more preferably, substantially no Li₂O or Na₂O is comprised.

(K₂O)

K₂O is a component which increases the basicity of a glass to impart refinability to the glass. K₂O is also a component which improves the meltability and decreases the specific resistance of a glass melt. Therefore, K₂O is not an essential component, but if K₂O is comprised, the specific resistance of a glass melt can be decreased and the clarity can be increased. However, if the amount of K₂O is excessively large, the coefficient of thermal expansion may increase, and the Tg and strain point may significantly decrease, leading to an excessive decrease in the heat resistance. Therefore, in the glass substrate of this embodiment, the K₂O content is preferably 0-0.8%, more preferably 0.01-0.5%, and even more preferably 0.1-0.3%.

(ZrO₂, TiO₂)

ZrO₂ and TiO₂ are components which increase the chemical durability and the Tg and strain point of a glass. ZrO₂ and TiO₂ are not essential components, but if ZrO₂ and TiO₂ are comprised, the Tg and strain point can be increased and the acid resistance can be improved. However, if the amounts of ZrO₂ and TiO₂ are excessively large, the devitrification temperature significantly increases, and therefore, the devitrification resistance and the ease of forming may decrease. In particular, crystals of ZrO₂ may precipitate in a cooling step, and these inclusions may cause a deterioration in the quality of the glass. TiO₂ is also a component which adds color to a glass, and therefore, is not suitable for display substrates. For these reasons, in the glass substrate of this embodiment, the ZrO₂ and TiO₂ contents are each preferably 0-5%, more preferably 0-3%, even more preferably 0-2%, still even more preferably 0-1%, and still even more preferably less than 0.5%. Still even more preferably, the glass substrate of this embodiment comprises substantially no ZrO₂ or TiO₂.

(ZnO)

ZnO is a component which improves the BHF resistance and meltability, and therefore, may be comprised, but is not an essential component. However, if the amount of ZnO is excessively large, the devitrification temperature may increase, the Tg and strain point may decrease, and the density may increase. Therefore, in the glass substrate of this embodiment, the ZnO content is preferably 5% or less, more preferably 3% or less, even more preferably 2% or less, and still even more preferably 1% or less. Still even more preferably, the glass substrate of this embodiment comprises substantially no ZnO. In other words, the ZnO content is preferably 0-5%, more preferably 0-3%, even more preferably 0-2%, and still even more preferably 0-1%. Still even more preferably, the glass substrate of this embodiment comprises substantially no ZnO.

(P₂O₅)

P₂O₅ is a component which decreases the melting temperature to improve the meltability, and therefore, may be comprised, but is not an essential component. However, if the amount of P₂O₅ is excessively large, P₂O₅ evaporates during melting of the glass, so that the non-uniformity of the glass becomes significant, and therefore, a cord is likely to occur. Also, it is likely that the Tg and strain point decreases, the acid resistance significantly deteriorates, and the glass turns into milky white. Therefore, in the glass substrate of this embodiment, the P₂O₅ content is preferably 3% or less, more preferably 1% or less, and even more preferably 0.5% or less. Still even more preferably, the glass substrate of this embodiment contains substantially no P₂O₅. In other words, the P₂O₅ content is preferably 0-3%, more preferably 0-1%, and even more preferably 0-0.5%. Still even more preferably, the glass substrate of this embodiment contains substantially no P₂O₅.

(Refining Agent)

Any refining agent that has low environmental load and imparts excellent clarity to a glass may be employed, i.e., the present invention is not limited to any particular refining agent. For example, the refining agent may be at least one selected from the group consisting of metal oxides of Sn, Fe, Ce, Tb, Mo, and W. If the amount of the refining agent is excessively small, the foam quality deteriorates. Therefore, the amount of the refining agent added is, for example, within the range of 0.01-1%, preferably 0.05-1%, more preferably 0.05-0.5%, even more preferably 0.05-0.3%, and still even more preferably 0.05-0.2%, although it depends on the type of the refining agent or the composition of the glass. The refining agent is preferably SnO₂. However, SnO₂ is a component which decreases the devitrification resistance of a glass. Therefore, for example, if SnO₂ is used as the refining agent, the SnO₂ content is preferably 0.01-0.3%, more preferably 0.03-0.2%, and even more preferably 0.05-0.15%.

(Fe₂O₃)

Fe₂O₃ is a component which works as a refining agent, and in addition, decreases the viscosity in a high-temperature region of a glass melt, and decreases the specific resistance. Fe₂O₃ is not an essential component, but is preferably comprised in a glass which has a high melting temperature and is therefore difficult to melt in order to decrease the melting temperature and specific resistance. If the amount of Fe₂O₃ is excessively large, color may be added to the glass, so that the transmittance may decrease. Therefore, in the glass substrate of this embodiment, the Fe₂O₃ content is preferably 0-0.1%, more preferably 0-0.08%, even more preferably 0.001-0.05%, and still even more preferably 0.005-0.03%. Here, in a glass having a high melting temperature, the temperature of the melting step is high, the effect of Fe₂O₃ as a refining agent is likely to decrease. Therefore, if Fe₂O₃ is used singly as a refining agent, the clarity may decrease, so that the foam quality of the glass substrate may deteriorate. Therefore, Fe₂O₃ is preferably used in combination with SnO₂.

In the glass substrate of this embodiment, in view of the environmental load problem, the Sb₂O₃ content is preferably 0-0.5%, more preferably 0-0.3%, even more preferably 0-0.1%, and still even more preferably 0-0.03%. Still even more preferably, the glass substrate of this embodiment contains substantially no Sb₂O₃.

(Components Preferably not Comprise)

In view of the environmental load problem, the glass substrate of this embodiment contains substantially no As₂O₃, Sb₂O₃, PbO, or F.

Also, compound parameters of components comprised in the glass substrate of this embodiment will be described hereinafter.

((SiO₂+Al₂O₃)/(B₂O₃))

In the glass included in the glass substrate of this embodiment, (SiO₂+Al₂O₃)/(B₂O₃) is preferably 7.5-17, more preferably 8-17, and even more preferably 8.45-17.0. By satisfying the relationship, the aforementioned advantages are obtained. Note that when the glass contains only less than 3% SrO+BaO in order to further reduce the weight, in order to reliably obtain the advantages (SiO₂+Al₂O₃)/(B₂O₃) is preferably 8.5-15.0, more preferably 9.5-14.0, even more preferably 10.0-13.0, and still even more preferably 10.0-12.5. Moreover, in order to prevent the increase of the devitrification temperature and achieve a sufficient etching rate, (SiO₂+Al₂O₃)/(B₂O₃) is preferably 8-15, more preferably 8-13, even more preferably 8-11, and still even more preferably 8-10. On the other hand, when the glass contains 3% or more SrO+BaO, (SiO₂+Al₂O₃)/(B₂O₃) is more preferably 9.5-17.0%, even more preferably 10.0-17.0%.

(Alkaline-Earth Metal Oxides (RO: MgO+CaO+SrO+BaO))

RO is a component which improves the meltability. If the amount of RO is excessively small, the meltability may deteriorate. However, if the amount of RO is excessively large, the Tg and strain point may decrease, the density may increase, the Young's modulus may decrease, and the coefficient of thermal expansion may increase. Therefore, in the glass included in the glass substrate of this embodiment, the RO content is preferably 3-25%, more preferably 4-20%. Note that when the glass contains only less than 3% SrO+BaO in order to further reduce the weight, the RO content is more preferably no less than 5% and less than 14%, even more preferably 6-14%, still even more preferably 8-13%, and still even more preferably 9-12%. On the other hand, when the glass contains 3% or more SrO+BaO, the RO content is more preferably no less than 5% and less than 18%, even more preferably 8-17%.

(CaO/RO)

When the glass contains only less than 3% SrO+BaO in order to further reduce the weight, CaO/RO is preferably 0.5 or more, more preferably 0.7 or more, even more preferably more than 0.85, still even more preferably 0.88 or more, still even more preferably 0.90 or more, still even more preferably 0.92 or more, and still even more preferably 0.95 or more. In other words, CaO/RO is preferably 0.5-1, more preferably 0.7-1, even more preferably more than 0.85 to 1, still even more preferably 0.88-1, still even more preferably 0.90-1, still even more preferably 0.92-1, and still even more preferably 0.95-1. If CaO/RO is within such a range, good devitrification resistance and meltability can be simultaneously obtained. Moreover, the density can be reduced. If only CaO is comprised as a material, the Tg and strain point can be further increased than when a plurality of alkaline-earth metal oxides are comprised. Note that even if only CaO, which is an alkaline-earth metal oxide, is comprised as a material, the obtained glass may contain another alkaline-earth metal oxide as an impurity. If only CaO, which is an alkaline-earth metal oxide, is comprised as a material, the value of CaO/RO of the obtained glass is, for example, about 0.98-1. CaO is also a preferable component because a material for CaO is inexpensive and easily available.

(SiO₂—(Al₂O₃/2))

If the value of SiO₂—(Al₂O₃/2) is excessively small, the etching rate may increase, but the devitrification resistance may decrease. On the other hand, if the value is excessively large, the etching rate may decrease. Therefore, in the glass included in the glass substrate of this embodiment, SiO₂—(Al₂O₃/2) is preferably 69 or less, more preferably 50-68, even more preferably 55-65, still even more preferably 57-63, and still even more preferably 58-62.

In order to perform etching (slimming) the glass substrate with a high productivity, the etching rate is preferably 50 μm/h or more. On the other hand, if the etching rate is excessively high, a problem is likely to occur in a reaction with a chemical solution in a panel production step. Therefore, for the glass included in the glass substrate, the etching rate is preferably 160 μm/h or less. The etching rate is preferably 60-140 μm/h, more preferably 70-120 μm/h. In the present invention, the etching rate is defined as being measured under the following conditions.

The etching rate (μm/h) is represented by the amount of a decrease in the thickness of one surface of the glass substrate per unit time (one hour), where the glass substrate is immersed in an etchant (an acid mixture of HF (concentration: 1 mol/kg) and HCl (concentration: 5 mol/kg)) at 40° C. for 1 hour.

(SiO₂+Al₂O₃)

If SiO₂+Al₂O₃ is excessively small, the Tg and strain point are likely to decrease. On the other hand, if SiO₂+Al₂O₃ is excessively large, the devitrification resistance is likely to deteriorate. Therefore, in the glass included in the glass substrate of this embodiment, SiO₂+Al₂O₃ is preferably 70% or more, more preferably 75% or more, and even more preferably 76-88%. Note that when the glass contains only less than 3% SrO+BaO in order to further reduce the weight, SiO₂+Al₂O₃ is more preferably 78-88%, even more preferably 79-85%, and still even more preferably 80-84%. Moreover, in order to prevent the increase of the devitrification temperature, SiO₂+Al₂O₃ is more preferably 76-85%, even more preferably 76-83%, and still even more preferably 78-82%. On the other hand, when the glass contains 3% or more SrO+BaO, SiO₂+Al₂O₃ is more preferably 76-86%, even more preferably 77-83%.

(Al₂O₃/SiO₂)

If Al₂O₃/SiO₂ exceeds 0.35, the devitrification resistance is likely to deteriorate. On the other hand, if Al₂O₃/SiO₂ is 0.05 or less, the Tg and strain point cannot be sufficiently increased. Therefore, in this embodiment, Al₂O₃/SiO₂ is 0.05-0.35, preferably 0.07-0.30, and more preferably 0.10-0.25.

(B₂O₃+P₂O₅)

If B₂O₃+P₂O₅ is excessively small, the meltability is likely to decrease. On the other hand, if B₂O₃+P₂O₅ is excessively large, B₂O₃+P₂O₅ evaporates during melting of the glass, so that the non-uniformity of the glass becomes significant, and therefore, a cord is likely to occur. Moreover, the Tg and strain point are likely to decrease. Therefore, in the glass included in the glass substrate of this embodiment, B₂O₃+P₂O₅ is preferably 3-15%, more preferably 3-10%. Note that when the glass contains only less than 3% SrO+BaO in order to further reduce the weight, B₂O₃+P₂O₅ is more preferably no less than 3% and less than 9.5%, even more preferably no less than 4% and less than 8.9%, still even more preferably 5-8.5%, and still even more preferably 6-8%. Moreover, in order to improve the devitrification resistance, B₂O₃+P₂O₅ is more preferably 5-13%, even more preferably 5-12%, still even more preferably 6% to less than 10% (no less than 6% and less than 10%). On the other hand, when the glass contains 3% or more SrO+BaO, B₂O₃+P₂O₅ is more preferably 3-9%, even more preferably 4-8%.

(CaO/B₂O₃)

Note that when the glass contains only less than 3% SrO+BaO in order to further reduce the weight, then if CaO/B₂O₃ is excessively low, the Tg and strain point are likely to decrease. On the other hand, if CaO/B₂O₃ is excessively high, the meltability is likely to deteriorate. Therefore, in this embodiment, CaO/B₂O₃ is preferably 0.5 or more, more preferably 0.7 or more, even more preferably 0.9 or more, still even more preferably more than 1.2, still even more preferably more than 1.2 and no more than 5, still even more preferably more than 1.2 and no more than 3, still even more preferably 1.3 or more and 2.5 or less, and still even more preferably 1.3 or more and 2 or less. Moreover, in order to improve the meltability, CaO/B₂O₃ is preferably 0.5-5, more preferably 0.9-3, even more preferably more than 1 and no more than 2.5, still even more preferably more than 1 and no more than 2, still even more preferably more than 1.2 and no more than 2, and still even more preferably more than 1.2 and no more than 1.5.

(SrO+BaO)

SrO and BaO are components which can decrease the devitrification temperature of a glass. These components are not essential, but if these components are comprised, the devitrification resistance and meltability can be improved. However, if the amount of these components is excessively large, the density increases. Therefore, it is difficult to decrease the density and reduce the weight. Also, the coefficient of thermal expansion may increase. Therefore, in the glass included in the glass substrate of this embodiment, SrO+BaO is preferably 10% or less. Note that, in order to further reduce the weight, SrO+BaO is more preferably 5% or less, even more preferably less than 3%, and still even more preferably less than 2%. Still even more preferably, the glass included in the glass substrate of this embodiment contains substantially no SrO or BaO. In other words, SrO+BaO is preferably 0-10%. In order to further reduce the weight, SrO+BaO is more preferably 0-5%, even more preferably 0% to less than 3% (no less than 0% and less than 3%), still even more preferably 0% to less than 2% (no less than 0% and less than 2%), still even more preferably 0% to less than 1% (no less than 0% and less than 1%), and still even more preferably 0% to less than 0.5% (no less than 0% and less than 0.5%). Still even more preferably, the glass included in the glass substrate of this embodiment contains no SrO or BaO.

(RO+ZnO+B₂O₃)

If RO+ZnO+B₂O₃ is excessively small, the viscosity in a high-temperature region is likely to be high, and the clarity and glass meltability are likely to decrease. On the other hand, if RO+ZnO+B₂O₃ is excessively large, the Tg and strain point are likely to decrease. Therefore, in the glass included in the glass substrate of this embodiment, RO+ZnO+B₂O₃ is preferably 7-30%, more preferably 10⁻²⁷%. Note that when the glass contains only less than 3% SrO+BaO in order to further reduce the weight, RO+ZnO+B₂O₃ is more preferably 12-22%, even more preferably 14-21%, and still even more preferably 16-20%. Moreover, in order to improve the meltability, RO+ZnO+B₂O₃ is more preferably 12-27%, even more preferably 14-25%, and still even more preferably 17-23%. On the other hand, when the glass contains 3% or more SrO+BaO, RO+ZnO+B₂O₃ is more preferably 13-27%, even more preferably 15-25%.

(Alkali Metal Oxide (R₂O: Li₂O+Na₂O+K₂O))

R₂O is a component which increases the basicity of a glass to facilitate oxidation of a refining agent, thereby imparting clarity to the glass. R₂O is also a component which facilitates improvement of the meltability of a glass and decrease of the specific resistance of the glass, and may be comprised. R₂O is not an essential component, but if it is comprised, can decrease the specific resistance and improve the clarity and meltability. However, if the amount of R₂O is excessively large, the Tg and strain point may excessively decrease, and the coefficient of thermal expansion may increase. Therefore, in the glass included in the glass substrate of this embodiment, R₂O is preferably 0-0.8%, more preferably 0.01-0.5%, and even more preferably 0.1-0.3%.

(K₂O/R₂O)

K₂O has a larger molecular weight than those of Li₂O and Na₂O, and therefore, runs off the glass substrate to a lesser extent. Therefore, if R₂O is comprised, K₂O is preferably comprised at a higher ratio. K₂O is preferably comprised at a higher ratio than that of Li₂O (K₂O>Li₂O is satisfied). K₂O is preferably comprised at a higher ratio than that of Na₂O (K₂O>Na₂O is satisfied). K₂O/R₂O is preferably 0.5 or more, more preferably 0.6 or more, even more preferably 0.7 or more, still even more preferably 0.8 or more, and still even more preferably 0.95 or more. In other words, K₂O/R₂O is preferably 0.5-1, more preferably 0.6-1, even more preferably 0.7-1, still even more preferably 0.8-1, and still even more preferably 0.95-1.

The glass included in the glass substrate of this embodiment can be obtained by appropriately combining the above components. The combination of the components is not limited. Example combinations will be described hereinafter. The glass may contain

65-78% SiO₂

3-20% Al₂O₃

3-15% B₂O₃

0% to less than 2% (no less than 0% and less than 2%) MgO

3.6-16% CaO

0-2% SrO

0% to less than 1% (no less than 0% and less than 1%) BaO

where

the B₂O₃, P₂O₅, and CaO contents in mol % may satisfy relationships B₂O₃+P₂O₅=3-15% and CaO/B₂O₃>1.2.

Alternatively, the glass may contain

65-78% SiO₂

3-20% Al₂O₃

3-9.5% B₂O₃

0% to less than 2% (no less than 0% and less than 2%) MgO

3.6-16% CaO

0-2% SrO

substantially no BaO

where

the B₂O₃, P₂O₅, and CaO contents in mol % may satisfy relationships B₂O₃+P₂O₅=3-9.5% and CaO/B₂O₃>1.2.

The glass substrate of this embodiment is a substrate for displays. Specifically, the glass substrate of this embodiment is suitable as a flat panel display glass substrate on which the p-Si TFT is formed. The glass substrate of this embodiment is also suitable as a liquid crystal display glass substrate and an organic EL display glass substrate. In particular, the glass substrate of this embodiment is suitable as a p-Si TFT liquid crystal display glass substrate and organic EL display glass substrate. The glass substrate of this embodiment is suitable as a display glass substrate for mobile terminals for which a high resolution is required, among other things. Alternatively, the glass substrate of this embodiment is suitable as an oxide semiconductor thin film flat panel display glass substrate. More specifically, the glass substrate of this embodiment is suitable as a glass substrate used in a flat panel display which is produced by forming an oxide semiconductor thin film TFT on a substrate surface.

The size of the glass substrate of this embodiment can be appropriately adjusted, depending on the size of a display to which the glass substrate is applied, and therefore, is not particularly limited. The length in the width direction of the glass substrate is, for example, 500-3500 mm, preferably 1000-3500 mm, and more preferably 2000-3500 mm. The length in the longitudinal direction of the glass substrate, for example, 500-3500 mm, preferably 1000-3500 mm, and more preferably 2000-3500 mm. As the size of the glass substrate increases, the productivity of liquid crystal displays or organic EL displays is improved.

The thickness of the glass substrate of this embodiment can be appropriately adjusted, depending on the size of a display to which the glass substrate is applied, and therefore, is not particularly limited. However, if the glass substrate is excessively thin, the strength of the glass substrate itself decreases. For example, damage is likely to occur during production of a liquid crystal display. On the other hand, if the glass substrate is excessively thick, the glass substrate is not suitable for a display which is desired to be thinner. Also, if the glass substrate is excessively thick, the glass substrate has a heavy weight, and therefore, it is difficult to reduce the weight of a liquid crystal display. Therefore, the thickness of the glass substrate of this embodiment is preferably 0.1-1.1 mm, more preferably 0.1-0.7 mm, even more preferably 0.3-0.7 mm, and still even more preferably 0.3-0.5 mm.

The glass substrate of this embodiment is manufactured by a method including a melting step of melting a glass material to produce molten glass, a forming step of forming the molten glass into a glass plate, and an annealing step of annealing the glass plate. Note that the ratio of heat shrinkage of the glass plate is 75 ppm or less, preferably 60 ppm or less. The glass included in the glass substrate has a devitrification temperature of 1250° C. or less, and contains, as expressed in mol %, SiO₂ (55-80%), Al₂O₃ (3-20%), B₂O₃ (3-15%), RO (3-25%: the total amount of MgO, CaO, SrO, and BaO) as a glass composition. The SiO₂, Al₂O₃, and B₂O₃ contents in mol % satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17, preferably 8.45-17.0. In this case, the glass preferably has a strain point of 665° C. or more.

The glass substrate of this embodiment can be manufactured by a known method for manufacturing a glass substrate. Also, a known forming method can be used, and a float process or a downdraw process is preferable. In particular, the overflow downdraw process is preferable. The glass substrate formed by tThe glass substrate formed by the downdraw process has main surfaces which are made by hot forming by hot forming, and therefore, is considerably highly flat and smooth. Therefore, it is no longer necessary to polish the surface of the glass substrate after the forming, resulting in a reduction in manufacturing cost and an improvement in productivity. Moreover, both main surfaces of the glass substrate formed by the downdraw process have a uniform composition, and therefore, can be uniformly etched during an etching process. In addition, by forming by the downdraw process, the glass substrate can obtain a surface condition free from a microcrack. As a result, the strength of the glass substrate itself can be improved.

In order to manufacture the glass substrate having a heat shrinkage ratio of 75 ppm or less, preferably 60 ppm or less, it is desirable that conditions under which annealing is performed be adjusted as appropriate. For example, when the downdraw process is used, annealing is desirably performed while keeping the temperature of the glass plate within the temperature range of Tg° C. to Tg−100° C. for 20-120 sec. In other words, when the downdraw process is used, annealing is desirably performed so that the glass plate is cooled to the temperature range of Tg° C. to Tg−100° C. in 20-120 sec. If the time is less than 20 sec, the amount of heat shrinkage may not be sufficiently reduced. On the other hand, if the time exceeds 120 sec, the productivity decreases and the size of the glass manufacturing equipment (annealing furnace) increases. Therefore, in order to reduce the ratio of heat shrinkage while keeping the cost and productivity, annealing is preferably performed while keeping the temperature of the glass plate within the temperature range of Tg° C. to Tg−100° C. for 20-120 sec, more preferably 30-120 sec, and even more preferably 50-100 sec. In other words, annealing is preferably performed so that the glass plate is cooled to the temperature range of Tg° C. to Tg−100° C. in 20-120 sec, more preferably 30-120 sec, and even more preferably 50-100 sec. Alternatively, annealing is preferably performed so that the average rate of cooling a center portion of the glass plate within the temperature range of Tg° C. to Tg−100° C. is 50-300° C./min. If the average cooling rate exceeds 300° C./min, the amount of heat shrinkage may not be sufficiently reduced. On the other hand, if the average cooling rate is less than 50° C./min, the productivity decreases and the size of the glass manufacturing equipment (annealing furnace) increases. Therefore, the average cooling rate range for reducing the ratio of heat shrinkage while keeping the cost and productivity is preferably 50-300° C./min, more preferably 50-200° C./min, and even more preferably 60-120° C./min. On the other hand, by separately providing a heat shrinkage reduction treatment (off-line annealing) step after the annealing step, the ratio of heat shrinkage can be reduced. However, if the off-line annealing step is provided separately from the annealing step, the productivity decreases and the cost increases. Therefore, as described above, the heat shrinkage reduction treatment (off-line annealing) of controlling the rate of cooling the glass plate is more preferably performed in the annealing step so that the ratio of heat shrinkage falls within the predetermined range.

The water content of glass may be represented by a β-OH value. As the β-OH value decreases, the Tg and strain point tend to increase. On the other hand, as the β-OH value increases, the melting temperature tends to decrease. In order to simultaneously achieve both the increase of the Tg and strain point and the improvement of the meltability, the β-OH value is preferably 0.05-0.40 mm⁻¹, more preferably 0.10-0.35 mm⁻¹, even more preferably 0.10-0.30 mm⁻¹, and still even more preferably 0.10-0.25 mm⁻¹. The β-OH value can be adjusted by selecting the material. For example, the β-OH value can be increased and decreased by selecting a material having a high water content (e.g., a hydroxide material) or adjusting the content of a material (e.g., a chloride) which reduces the water content of a glass. The β-OH value can also be adjusted by adjusting the ratio of gas burning heating (oxygen burning heating) and electrical heating (direct electrical heating) for melting glass. The β-OH value can also be increased by increasing the amount of moisture in furnace atmosphere or bubbling water vapor with respect to molten glass during the melting. Note that the β-OH value of a glass is calculated based on the infrared absorption spectrum of the glass by the following expression:

β-OH value=(1/X)log 10(T1/T2)

X: glass thickness (mm)

T1: transmittance (%) at a reference wavelength of 2600 nm

T2: minimum transmittance (%) in the vicinity of a hydroxyl group absorption wavelength of 2800 nm

As examples of the flat panel display glass substrate of this embodiment obtained from the present disclosure, first to fourth glass substrates will be described hereinafter. As examples of the method for manufacturing the glass substrate of this embodiment obtained from the present disclosure, first to fourth manufacturing methods will be described hereinafter.

The first flat panel display glass substrate includes a glass comprising, as expressed in mol %:

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17,

the strain point of the glass is 665° C. or more, and

the devitrification temperature of the glass is 1250° C. or less, and

the ratio of heat shrinkage of the glass substrate is 75 ppm or less.

The second flat panel display glass substrate includes a glass comprising, as expressed in mol %:

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

RO (the total amount of MgO, CaO, SrO, and BaO) 3-25%

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0, and

the devitrification temperature of the glass is 1250° C. or less, and

the ratio of heat shrinkage of the glass substrate is 60 ppm or less.

The third flat panel display glass substrate includes a glass comprising, as expressed in mol %,

65-78% SiO₂

3-20% Al₂O₃

3-15% B₂O₃

0% to less than 2% MgO

3.6-16% CaO

0-2% SrO

0% to less than 1% BaO

where

the contents in mol % of B₂O₃, P₂O₅, and CaO satisfy relationships B₂O₃+P₂O₅=3-15% and CaO/B₂O₃>1.2,

the strain point of the glass is 665° C. or more, and

the devitrification temperature of the glass is 1250° C. or less.

The fourth flat panel display glass substrate includes a glass comprising, as expressed in mol %,

65-78% SiO₂

3-20% Al₂O₃

3-9.5% B₂O₃

0% to less than 2% MgO

3.6-16% CaO

0-2% SrO

substantially no BaO

where

the contents in mol % of B₂O₃, P₂O₅, and CaO satisfy relationships B₂O₃+P₂O₅=3-9.5% and CaO/B₂O₃>1.2, and

the devitrification temperature of the glass is 1250° C. or less.

The first to fourth flat panel display glass substrates are suitable as flat panel display glass substrates on which the p-Si TFT is formed. In particular, the first to fourth flat panel display glass substrates are suitable as liquid crystal display glass substrates on which the p-Si TFT is formed. Alternatively, the first to fourth flat panel display glass substrates are also suitable as organic EL display glass substrates. Alternatively, the first to fourth flat panel display glass substrates are suitable as display glass substrates on which an oxide semiconductor thin film transistor is formed.

The first method for manufacturing a flat panel display glass substrate includes

a melting step of melting a glass material for a glass comprising, as expressed in mol %, 55-80% SiO₂, 3-20% Al₂O₃, 3-15% B₂O₃, and 3-25% RO (the total amount of MgO, CaO, SrO, and BaO), with the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfying a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17.0, the strain point of the glass being 665° C. or more, and the devitrification temperature of the glass being 1250° C. or less, to produce a molten glass,

a forming step of forming the molten glass into a glass plate, and

an annealing step of annealing the glass plate, where

the rate of heat shrinkage of the glass plate is 75 ppm or less.

The second method for manufacturing a flat panel display glass substrate includes

a melting step of melting a glass material for a glass comprising, as expressed in mol %, 55-80% SiO₂, 3-20% Al₂O₃, 3-15% B₂O₃, and 3-25% RO (the total amount of MgO, CaO, SrO, and BaO), with the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfying a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0 and the devitrification temperature of the glass being 1250° C. or less, to produce a molten glass,

a forming step of forming the molten glass into a glass plate, and

an annealing step of annealing the glass plate, where

the rate of heat shrinkage of the glass plate is 60 ppm or less.

The third method for manufacturing a flat panel display glass substrate includes

a melting step of melting a glass material for a glass comprising, as expressed in mol %, 65-78% SiO₂, 3-20% Al₂O₃, 3-15% B₂O₃, 0% to less than 2% MgO, 3.6-16% CaO, 0-2% SrO, and 0% to less than 1% BaO, with the contents in mol % of B₂O₃, P₂O₃, and CaO satisfying relationships B₂O₃+P₂O₅=3-15% and CaO/B₂O₃>1.2, the strain point of the glass being 665° C. or more, and the devitrification temperature of the glass being 1250° C. or less, to produce a molten glass,

a forming step of forming the molten glass into a glass plate, and

an annealing step of annealing the glass plate.

The fourth method for manufacturing a flat panel display glass substrate includes

a melting step of melting a glass material for a glass comprising, as expressed in mol %, 65-78% SiO₂, 3-20% Al₂O₃, 3-9.5% B₂O₃, 0% to less than 2% MgO, 3.6-16% CaO, 0-2% SrO, and substantially no BaO, with the contents in mol % of B₂O₃, P₂O₃, and CaO satisfying relationships B₂O₃+P₂O₅=3-9.5% and CaO/B₂O₃>1.2 and the devitrification temperature of the glass being 1250° C. or less, to produce a molten glass,

a forming step of forming the molten glass into a glass plate, and

an annealing step of annealing the glass plate.

In the annealing steps of the first to fourth manufacturing methods of the flat panel display glass substrate, a heat shrinkage reduction treatment for reducing the rate of heat shrinkage is preferably performed by controlling the rate of cooling the glass plate. Also, in the annealing steps, the heat shrinkage reduction treatment is more preferably performed so that the average cooling rate of a center portion of the glass plate within the temperature range of Tg° C. to Tg−100° C. is 50-300° C./min.

EXAMPLES

Next, the glass substrate of the present invention will be described in detail by way of example. Note that the present invention is not intended to be limited to examples described below.

<First Glass Substrate>

The first glass substrate will be described by way of example. Note that the first glass substrate includes a glass comprising, as expressed in mol %:

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17,

the strain point of the glass is 665° C. or more, and

the devitrification temperature of the glass is 1250° C. or less, and

the rate of heat shrinkage of the glass substrate is 75 ppm or less.

Examples 1-1 to 1-24 and Comparative Examples 1-1 to 1-6

Sample glasses of Examples 1-1 to 1-24 and Comparative Examples 1-1 to 1-6 were produced by a procedure described below so that the sample glasses have glass compositions shown in Tables 1-1 and 1-2. For the obtained sample glasses and sample glass substrates, devitrification temperature, Tg, average coefficient of thermal expansion within the range of 100-300° C., rate of heat shrinkage, density, strain point, melting temperature (glass temperature where viscosity is 10^(2.5) dPa·s), liquidus viscosity, and specific resistance at 1550° C., were measured.

(Production of Sample Glass)

Initially, glass material batches (hereinafter referred to as “batches”) having glass compositions shown in Tables 1-1 and 1-2 were prepared using typical glass materials, i.e., silica, alumina, boron oxide, potassium carbonate, basic magnesium carbonate, calcium carbonate, strontium carbonate, tin dioxide, and iron(III) oxide, in amounts which would provide 400 g of a glass.

The prepared batch was melted, followed by refining, in a platinum crucible. Initially, the crucible was held for 4 hours in an electrical furnace which was set to 1575° C. to melt the batch. Next, the temperature of the electrical furnace was increased to 1640° C., and the platinum crucible was held for 2 hours to perform refining on the glass melt. Thereafter, the glass melt was poured onto an iron plate outside the furnace, and was cooled and solidified to obtain a glass piece. Following this, an annealing process was performed on the glass piece. In the annealing process, the glass piece was held for 2 hours in another electrical furnace which was set to 800° C., and thereafter, cooled for 2 hours until the temperature dropped to 740° C., and further cooled for 2 hours until the temperature dropped to 660° C. Thereafter, the electrical furnace was turned off, and the glass piece was cooled to room temperature. The glass piece after the annealing process was a sample glass. The sample glass was used to measure properties (devitrification temperature, melting temperature, specific resistance, density, coefficient of thermal expansion, and Tg and strain point), which are not affected by annealing conditions and/or cannot be measured in the form of a substrate.

The sample glass was cut, ground, and polished to produce a sample glass substrate of 30 mm×40 mm×0.7 mm whose top and bottom surfaces are a mirror surface. The sample glass substrate was used to measure β-OH, which is not affected by annealing conditions.

Moreover, the sample glass substrate was formed into a rectangular parallelepiped having a width of 5 mm and a length of 20 mm by a commonly used glass processing technique. The resulting sample glass substrate was kept at Tg for 30 min, and thereafter, cooled at a rate of 100° C./min until the temperature reached Tg−100° C. and then cooled until the temperature reached room temperature. The sample glass substrate for measurement of heat shrinkage was thus prepared.

(Method for Measuring Devitrification Temperature)

The sample glass was pulverized, and was passed through a 2380-μm sieve. Glass particles which were retained on a 1000-μm sieve were obtained. The glass particles were immersed in ethanol, followed by ultrasonic cleaning and then drying in a constant temperature bath. Twenty-five grams of the dried glass particles were placed to substantially a uniform thickness in a platinum boat having a width of 12 mm, a length of 200 mm, and a depth of 10 mm. The platinum boat was held for 5 hours in an electrical furnace having a temperature gradient of 1080-1320° C. (for Examples 1-1 to 1-6, 1-8 to 1-24 and Comparative Examples 1-1 and 1-3 to 1-5) or 1140-1380° C. (for Examples 1-7 and Comparative Examples 1-2 and 1-6). Thereafter, the platinum boat was removed from the furnace. Devitrification occurring inside the glass was observed by a 50× optical microscope. A highest temperature at which devitrification was observed was defined as a devitrification temperature.

(Melting Temperature)

The melting temperature of the sample glass was measured using a platinum sphere dragging type automatic viscometer. A temperature at which the viscosity was 10^(2.5) dPa·s was calculated from the measurement result, and was defined as the melting temperature.

(Liquidus Viscosity)

A viscosity at the devitrification temperature was calculated from the measurement result of the melting temperature, and was defined as a liquidus viscosity.

(Specific Resistance)

The specific resistance of the sample glass as it is melted was measured by four-terminal sensing using the 4192A LF impedance analyzer (manufactured by HP). The specific resistance value at 1550° C. was calculated from the measurement result.

(Method for Measuring Average Coefficient of Thermal Expansion and Tg within Range of 100-300° C.)

The sample glass was processed into the form of a cylinder having a diameter (φ) of 5 mm and a length of 20 mm, and was used as a test piece. The temperature and the amount of expansion/shrinkage of the test piece were measured in the process of increasing the temperature of the test piece using a differential thermal dilatometer (Thermo Plus2 TMA8310). In this case, the rate of increasing the temperature was 5° C./min. The average coefficient of thermal expansion and the Tg within the temperature range of 100-300° C. were measured based on the measurement results of the temperature and the amount of expansion/shrinkage of the test piece. Note that the Tg as used herein refers to a value of a sample glass which was measured by holding a glass piece in another electrical furnace which was set to 800° C. for 2 hours, cooling the glass piece for 2 hours until the temperature dropped to 740° C., and then cooling the glass piece for 2 hours until the temperature dropped to 660° C., and thereafter, turning off the electrical furnace, and cooling the glass piece until the temperature dropped to room temperature.

(Strain Point)

The sample glass was cut and ground into the form of a prism having a 3-mm square base and a length of 55 mm, and was used as a test piece. The test piece was measured using a beam bending measurement device (manufactured by TokyoKogyo Co., Ltd.). The strain point was calculated by a beam bending technique (ASTM C-598).

(Density)

The sample glass was mirror-polished to produce a plate-like sample of 5×30×30 mm. This sample was used to measure the density of the glass using Archimedes' technique.

(Rate of Heat Shrinkage)

The rate of heat shrinkage was calculated from the amount of shrinkage of the glass substrate for measurement of heat shrinkage after a heat treatment at 550° C. for 2 hours using the following expression:

the rate of heat shrinkage (ppm)={the amount of shrinkage of the glass substrate after the heat treatment/the length of the glass substrate before the heat treatment}×10⁶

In this example, the amount of shrinkage was specifically measured by the following technique.

The heat shrinkage sample glass was heated from room temperature to 550° C. using a differential thermal dilatometer (Thermoflex TMA8140 manufactured by Rigaku Corporation), was held for 2 hours, and was cooled to room temperature. The amount of shrinkage of the sample glass between before and after the heat treatment was measured. In this case, the rate of increasing the temperature was 10° C./min.

(Etching Rate)

The glass substrate was immersed in an etchant (an acid mixture of HF (concentration: 1 mol/kg) and HCl (concentration: 5 mol/kg)) at 40° C. for 1 hour. Thereafter, a reduction (μm) in the thickness of one surface of the glass substrate was measured. The reduction (μm) per unit time (one hour) was defined as an etching rate (μm/h).

TABLE 1-1 Examples 1-1 1-2 1-3 1-4 1-5 1-6 1-7 1-8 Compo- SiO₂ 71.7 71.6 70.8 70.5 70.5 70.3 69.4 69.7 sition B₂O₃ 6.0 6.0 6.9 7.4 7.4 7.8 8.7 9.7 (mol %) Al₂O₃ 11.1 11.1 11.0 10.9 10.9 10.9 10.8 10.8 K₂O 0.17 0.17 0.17 0.17 0.40 MgO 1.0 CaO 11.1 11.1 11.0 10.9 9.9 10.9 9.8 8.9 SrO 0.8 0.8 BaO SnO₂ 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 Fe₂O₃ 0.022 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 13.8 13.8 11.8 11.0 11.0 10.3 9.2 8.3 B₂O₃ SiO₂ + Al₂O₃ 82.8 82.6 81.8 81.4 81.4 81.2 80.2 80.5 RO + B₂O₃ + 17.1 17.1 17.9 18.3 18.3 18.7 19.3 19.4 ZnO Al₂O₃/SiO₂ 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 RO 11.1 11.1 11.0 10.9 10.9 10.9 10.6 9.7 B₂O₃ + P₂O₅ 6.0 6.0 6.9 7.4 7.4 7.8 8.7 9.7 CaO/RO 1 1 1 1 0.91 1 0.93 0.92 SiO₂—Al₂O₃/2 66.1 66.0 65.4 65.0 65.0 64.8 64.1 64.3 β-OH 0.11 0.12 0.11 0.11 0.12 0.13 0.13 0.11 Properties devitrification 1233 1230 1213 1189 1206 1187 <1140 1151 temperature (° C.) Tg (° C.) 782 776 766 758 751 761 741 745 average coeffi- 34.2 34.0 32.9 32.6 33.1 33.2 36.3 29.6 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 31 36 44 48 52 46 40 32 shrinkage (ppm) density (g/cm³) 2.41 2.41 2.40 2.39 2.39 2.38 2.40 2.37 strain point (° C.) 723 716 707 709 704 707 685 695 melting 1644 1632 1620 1608 1609 1610 1644 1650 temperature (° C.) liquidus viscosity 5.0 5.0 5.1 5.2 5.0 5.2 5.3 5.5 (log η) specific resistance 243 193 194 195 194 248 170 253 (Ω · cm) (1550° C.) etching rate (μm/h) 65 65 67 69 69 69 72 71 Examples 1-9 1-10 1-11 1-12 1-13 1-14 1-15 Compo- SiO₂ 67.2 66.7 69.7 67.5 67.3 67.8 66.9 sition B₂O₃ 4.7 5.0 5.0 7.5 8.3 7.8 9.2 (mol %) Al₂O₃ 12.5 13.2 12.2 12.9 12.7 12.5 12.2 K₂O 0.17 0.17 0.17 0.20 0.17 0.17 0.17 MgO 6.9 7.4 5.8 CaO 1.7 1.3 1.42 11.7 11.5 11.5 11.4 SrO 6.8 6.2 5.7 BaO SnO₂ 0.09 0.09 0.09 0.10 0.08 0.08 0.08 Fe₂O₃ 0.02 0.02 0.02 0.02 (SiO₂ + Al₂O₃)/ 17.0 16.0 16.4 10.7 9.7 10.3 8.6 B₂O₃ SiO₂ + Al₂O₃ 79.7 79.9 81.9 80.4 80.0 80.4 79.2 RO + B₂O₃ + 20.1 19.9 17.9 19.2 19.8 19.4 20.5 ZnO Al₂O₃/SiO₂ 0.19 0.20 0.18 0.19 0.19 0.18 0.18 RO 15.4 14.9 12.9 11.7 11.5 11.5 11.4 B₂O₃ + P₂O₅ 4.7 5.0 5.0 7.5 8.3 7.8 9.2 CaO/RO 0.11 0.09 0.11 1 1 1 1 SiO₂—Al₂O₃/2 61.0 60.1 63.6 61.1 61.0 61.6 60.8 β-OH 0.13 0.13 0.14 0.12 0.11 0.11 0.10 Properties devitrification 1241 1219 1215 1230 1220 1236 1193 temperature (° C.) Tg (° C.) 749 764 768 763 754 760 741 average coeffi- 39.8 36.4 33.6 36.0 35.9 36.0 36.1 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 42 29 27 28 33 31 40 shrinkage (ppm) density (g/cm³) 2.58 2.55 2.52 2.40 2.41 2.42 2.40 strain point (° C.) 694 712 711 712 702 710 695 melting 1532 1538 1553 1587 1582 1579 1567 temperature (° C.) liquidus viscosity 4.3 4.5 4.7 4.6 4.7 4.6 4.9 (log η) specific resistance 203 203 236 137 133 129 142 (Ω · cm) (1550° C.) etching rate (μm/h) 83 85 73 80 82 80 83

TABLE 1-2 Examples 1-16 1-17 1-18 1-19 1-20 1-21 1-22 1-23 1-24 Compo- SiO₂ 67.64 72.0 66.5 66.5 66.5 63.5 70.5 70.5 70.5 sition B₂O₃ 7.83 6.4 9.5 9.5 4.5 4.5 7.4 7.4 7.4 (mol %) Al₂O₃ 12.73 11.4 11.4 12.4 10.4 10.4 10.9 10.9 10.9 K₂O 0.17 0.17 0.17 0.17 0.17 0.17 0.17 0.17 0.17 MgO 2.0 CaO 6.5 9.9 12.3 11.3 18.3 21.3 8.9 9.9 8.9 SrO 5 1.0 2.0 BaO SnO₂ 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 Fe₂O₃ 0.022 0.022 0.022 0.022 0.022 0.022 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 10.3 13.1 8.2 8.3 16.9 16.2 11.0 11.0 11.0 B₂O₃ SiO₂ + Al₂O₃ 80.4 83.4 77.9 78.9 76.9 73.9 81.4 81.4 81.4 RO + B₂O₃ + 19.4 16.3 21.8 20.8 22.8 25.8 18.3 18.3 18.3 ZnO Al₂O₃/SiO₂ 0.19 0.16 0.17 0.19 0.16 0.16 0.15 0.15 0.15 RO 11.5 9.9 12.3 11.3 18.3 21.3 10.9 10.9 10.9 B₂O₃ + P₂O₅ 7.83 6.4 9.5 9.5 4.5 4.5 7.4 7.4 7.4 CaO/RO 0.57 1 1 1 1 1 0.82 0.91 0.82 SiO₂—Al₂O₃/2 61.3 66.3 60.7 60.2 61.2 58.2 65.0 65.0 65.0 β-OH 0.12 0.12 0.11 0.11 0.10 0.10 0.12 0.12 0.12 Properties devitrification 1221 1235 1196 1208 1228 1206 1201 1207 1200 temperature (° C.) Tg (° C.) 758 781 731 743 739 732 742 752 753 average coeffi- 38.2 33.3 37.2 36 46.8 50.9 30.4 35.0 35.8 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 33 23 47 39 49 54 39 34 33 shrinkage (ppm) density (g/cm³) 2.48 2.38 2.40 2.40 2.50 2.55 2.38 2.41 2.42 strain point (° C.) 703 731 681 693 689 682 695 702 703 melting 1595 1640 1554 1560 1548 1541 1614 1610 1608 temperature (° C.) liquidus viscosity 4.8 4.9 4.7 4.6 4.3 4.4 5.1 5.0 5.1 (log η) specific resistance 138 207 179 191 108 73 193 196 197 (Ω · cm) (1550° C.) etching rate (μm/h) 83 64 83 85 81 92 69 69 69 Comparative Examples 1-1 1-2 1-3 1-4 1-5 1-6 Compo- SiO₂ 71.7 71.7 66.4 67.64 67.64 67.64 sition B₂O₃ 4.0 11.0 7.83 7.83 7.83 (mol %) Al₂O₃ 11.1 11.1 10.9 12.73 12.73 12.73 K₂O 0.18 0.17 0.17 0.17 MgO 2.8 1 3 5 CaO 13.1 17.1 6.8 10.5 8.5 6.5 SrO 1.69 BaO SnO₂ 0.08 0.09 0.09 0.08 0.08 0.08 Fe₂O₃ 0.03 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 20.7 7.0 10.3 10.3 10.3 B₂O₃ SiO₂ + Al₂O₃ 82.8 82.8 77.4 80.4 80.4 80.4 RO + B₂O₃ + 17.1 17.1 22.3 19.4 19.4 19.4 ZnO Al₂O₃/SiO₂ 0.15 0.15 0.16 0.19 0.19 0.19 RO 13.1 17.1 11.3 11.5 11.5 11.5 B₂O₃ + P₂O₅ 4.0 11.0 7.83 7.83 7.83 CaO/RO 1 1 0.60 0.91 0.74 0.57 SiO₂—Al₂O₃/2 66.1 66.1 61.0 61.3 61.3 61.3 β-OH 0.13 0.11 0.11 0.11 0.11 0.12 Properties devitrification 1282 1330 1196 1260 1294 1324 temperature (° C.) Tg (° C.) 786 826 707 758 749 746 average coeffi- 29.8 41.0 34.3 34.4 33.3 32.8 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 17 13 114 32 37 38 shrinkage (ppm) density (g/cm³) 2.445 2.510 2.40 2.41 2.40 2.40 strain point (° C.) 725 774 660 708 697 691 melting 1675 1701 1529 1585 1580 1577 temperature (° C.) liquidus viscosity 4.7 4.4 4.6 4.4 4.2 4.0 (log η) specific resistance 230 188 165 132 130 128 (Ω · cm) (1550° C.) etching rate (μm/h) 65 65 82 83 81 79

The glass substrates of Examples 1-1 to 1-24 had a Tg of 720° C. or more, and the rate of heat shrinkage and devitrification temperature thereof satisfied the conditions of the first glass substrate of the present invention. The glasses of Examples 1-1 to 1-24 had a melting temperature of 1680° C. or less, i.e., good meltability. Therefore, the glass substrates of Examples 1-1 to 1-24 have excellent properties and can be used in displays to which the p-Si TFT is applied. On the other hand, the ratios of heat shrinkage or devitrification temperatures of the glasses of Comparative Examples 1-1 to 1-6 did not satisfy the conditions of the first glass substrate of the present invention. The melting temperature of the glass of Comparative Example 2 exceeded 1680° C., i.e., good meltability was not obtained. Thus, the glass substrates of Comparative Examples 1-1 to 1-6 were not suitable for displays to which the p-Si TFT is applied.

Example 1-25

A glass material prepared to have a composition shown in Example 1-4 was melted at 1560-1640° C., followed by refining at 1620-1670° C. and then stirring at 1440-1530° C., using continuous melting equipment including a melting bath of fire bricks and a refining bath (adjustment bath) of a platinum alloy. Thereafter, the glass material was formed into a thin plate having a thickness of 0.7 mm by the overflow downdraw process, followed by cooling at an average rate of 100° C./min within the temperature range of Tg° C. to Tg−100° C., thereby obtaining a glass substrate for liquid crystal displays (or organic EL displays). Note that the aforementioned properties of the obtained glass substrate were measured. Note that, for properties (density, strain point, expansion coefficient, and Tg) which cannot be measured in the form of a substrate, the glass substrate was melted again to produce a sample glass according to the aforementioned sample production process, and the properties of the sample glass were measured.

The glass substrate of Example 1-25 thus obtained had a melting temperature of 1610° C., a β-OH value of 0.20 mm⁻¹, a Tg of 754° C., a strain point of 697° C., and a heat shrinkage rate of 51 ppm, and the other properties thereof were similar to those of Example 1-4. Thus, the glass substrate of Example 1-25 had a Tg of 720° C. or more and a melting temperature of 1680° C. or less, i.e., a high Tg and strain point and good meltability. Moreover, the rate of heat shrinkage and devitrification temperature satisfied the conditions of the first glass substrate of the present invention. Note that the glass substrate of Example 1-25 has a β-OH value which is greater than that of Example 1-4 by about 0.1 mm⁻¹, and therefore, has a Tg which is lower than that of Example 1-4 by 2-3° C., and the Tg is still sufficiently high. Therefore, the glass substrate of Example 1-25 has excellent properties and can be used in displays to which the p-Si TFT is applied.

Example 1-26

A glass substrate was produced using a glass material prepared to have a glass composition shown in Example 1-12 in a manner similar to that of Example 1-25, and the properties of the glass substrate were measured.

The glass substrate of Example 1-26 thus obtained had a melting temperature of 1585° C., a β-OH value of 0.21 mm⁻¹, a Tg of 761° C., a strain point of 710° C., and a heat shrinkage rate of 31 ppm, and the other properties thereof were similar to those of Example 1-12. Thus, the glass substrate of Example 1-26 had a Tg of 720° C. or more and a melting temperature of 1680° C. or less, i.e., a high Tg and strain point and good meltability. Moreover, the rate of heat shrinkage and devitrification temperature satisfied the conditions of the first glass substrate of the present invention. Note that the glass substrate of Example 1-26 has a β-OH value which is greater than that of Example 1-12 by about 0.1 mm⁻¹, and therefore, has a Tg which is lower than that of Example 1-12 by 2-3° C., and the Tg is still sufficiently high. Therefore, the glass substrate of Example 1-26 has excellent properties and can be used in displays to which the p-Si TFT is applied.

<Second Glass Substrate>

The second glass substrate will be described by way of example. Note that the second glass substrate includes a glass comprising, as expressed in mol %;

55-80% SiO₂;

3-20% Al₂O₃;

3-15% B₂O₃; and

3-25% RO (the total amount of MgO, CaO, SrO, and BaO)

wherein

in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0, and

the devitrification temperature of the glass is 1250° C. or less, and

the rate of heat shrinkage is 60 ppm or less.

Examples and comparative examples of the sample glass having glass compositions shown in Tables 2-1 and 2-2 were produced in a manner similar to that of the examples and comparative examples of the first glass substrate, and the properties thereof were measured.

TABLE 2-1 Examples 2-1 2-2 2-3 2-4 2-5 2-6 2-7 2-8 Compo- SiO₂ 71.7 71.6 70.8 70.5 70.5 70.3 69.4 67.2 sition B₂O₃ 6.0 6.0 6.9 7.4 7.4 7.8 8.7 4.7 (mol %) Al₂O₃ 11.1 11.1 11.0 10.9 10.9 10.9 10.8 12.5 K₂O 0.17 0.17 0.17 0.17 0.40 0.17 MgO 1.0 6.9 CaO 11.1 11.1 11.0 10.9 9.9 10.9 9.8 1.7 SrO 0.8 6.8 BaO SnO₂ 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.09 Fe₂O₃ 0.022 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 13.8 13.8 11.8 11.0 11.0 10.3 9.2 17.0 B₂O₃ SiO₂ + Al₂O₃ 82.8 82.6 81.8 81.4 81.4 81.2 80.2 79.7 RO + B₂O₃ + 17.1 17.1 17.9 18.3 18.3 18.7 19.3 20.1 ZnO Al₂O₃/SiO₂ 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.19 RO 11.1 11.1 11.0 10.9 10.9 10.9 10.6 15.4 B₂O₃ + P₂O₅ 6.0 6.0 6.9 7.4 7.4 7.8 8.7 4.7 CaO/RO 1 1 1 1 0.91 1 0.93 0.11 SiO₂—Al₂O₃/2 66.1 66.0 65.4 65.0 65.0 64.8 64.1 61.0 β-OH 0.11 0.12 0.11 0.11 0.12 0.13 0.13 0.13 Properties devitrification 1233 1230 1213 1189 1206 1187 <1140 1241 temperature (° C.) Tg (° C.) 782 776 766 758 751 761 741 749 average coeffi- 34.2 34.0 32.9 32.6 33.1 33.2 36.3 39.8 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 31 36 44 48 52 46 40 42 shrinkage (ppm) density (g/cm³) 2.41 2.41 2.40 2.39 2.39 2.38 2.40 2.58 strain point (° C.) 723 716 707 709 704 707 685 694 melting 1644 1632 1620 1608 1609 1610 1644 1532 temperature (° C.) liquidus viscosity 5.0 5.0 5.1 5.2 5.0 5.2 5.3 4.3 (log η) specific resistance 243 193 194 195 194 248 170 203 (Ω · cm) (1550° C.) etching rate (μm/h) 65 65 67 69 69 69 72 83 Examples 2-9 2-10 2-11 2-12 2-13 2-14 2-15 Compo- SiO₂ 66.7 69.7 67.5 67.3 67.8 66.9 67.64 sition B₂O₃ 5.0 5.0 7.5 8.3 7.8 9.2 7.83 (mol %) Al₂O₃ 13.2 12.2 12.9 12.7 12.5 12.2 12.73 K₂O 0.17 0.17 0.20 0.17 0.17 0.17 0.17 MgO 7.4 5.8 CaO 1.3 1.42 11.7 11.5 11.5 11.4 6.5 SrO 6.2 5.7 5 BaO SnO₂ 0.09 0.09 0.10 0.08 0.08 0.08 0.08 Fe₂O₃ 0.02 0.02 0.02 0.02 0.022 (SiO₂ + Al₂O₃)/ 16.0 16.4 10.7 9.7 10.3 8.6 10.3 B₂O₃ SiO₂ + Al₂O₃ 79.9 81.9 80.4 80.0 80.4 79.2 80.4 RO + B₂O₃ + 19.9 17.9 19.2 19.8 19.4 20.5 19.4 ZnO Al₂O₃/SiO₂ 0.20 0.18 0.19 0.19 0.18 0.18 0.19 RO 14.9 12.9 11.7 11.5 11.5 11.4 11.5 B₂O₃ + P₂O₅ 5.0 5.0 7.5 8.3 7.8 9.2 7.83 CaO/RO 0.09 0.11 1 1 1 1 0.57 SiO₂—Al₂O₃/2 60.1 63.6 61.1 61.0 61.6 60.8 61.3 β-OH 0.13 0.14 0.12 0.11 0.11 0.10 0.12 Properties devitrification 1219 1215 1230 1220 1236 1193 1221 temperature (° C.) Tg (° C.) 764 768 763 754 760 741 758 average coeffi- 36.4 33.6 36.0 35.9 36.0 36.1 38.2 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 29 27 28 33 31 40 33 shrinkage (ppm) density (g/cm³) 2.55 2.52 2.40 2.41 2.42 2.40 2.48 strain point (° C.) 712 711 712 702 710 695 703 melting 1538 1553 1587 1582 1579 1567 1595 temperature (° C.) liquidus viscosity 4.5 4.7 4.6 4.7 4.6 4.9 4.8 (log η) specific resistance 203 236 137 133 129 142 138 (Ω · cm) (1550° C.) etching rate (μm/h) 85 73 80 82 80 83 83

TABLE 2-2 Examples 2-16 2-17 2-18 2-19 2-20 2-21 2-22 2-23 Compo- SiO₂ 72.0 66.5 66.5 66.5 63.5 70.5 70.5 70.5 sition B₂O₃ 6.4 9.5 9.5 4.5 4.5 7.4 7.4 7.4 (mol %) Al₂O₃ 11.4 11.4 12.4 10.4 10.4 10.9 10.9 10.9 K₂O 0.17 0.17 0.17 0.17 0.17 0.17 0.17 0.17 MgO 2.0 CaO 9.9 12.3 11.3 18.3 21.3 8.9 9.9 8.9 SrO 1.0 2.0 BaO SnO₂ 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 Fe₂O₃ 0.022 0.022 0.022 0.022 0.022 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 13.1 8.2 8.3 16.9 16.2 11.0 11.0 11.0 B₂O₃ SiO₂ + Al₂O₃ 83.4 77.9 78.9 76.9 73.9 81.4 81.4 81.4 RO + B₂O₃ + 16.3 21.8 20.8 22.8 25.8 18.3 18.3 18.3 ZnO Al₂O₃/SiO₂ 0.16 0.17 0.19 0.16 0.16 0.15 0.15 0.15 RO 9.9 12.3 11.3 18.3 21.3 10.9 10.9 10.9 B₂O₃ + P₂O₅ 6.4 9.5 9.5 4.5 4.5 7.4 7.4 7.4 CaO/RO 1 1 1 1 1 0.82 0.91 0.82 SiO₂—Al₂O₃/2 66.3 60.7 60.2 61.2 58.2 65.0 65.0 65.0 β-OH 0.12 0.11 0.11 0.10 0.10 0.12 0.12 0.12 Properties devitrification 1235 1196 1208 1228 1206 1201 1207 1200 temperature (° C.) Tg (° C.) 781 731 743 739 732 742 752 753 average coeffi- 33.3 37.2 36 46.8 50.9 30.4 35.0 35.8 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 23 47 39 49 54 39 34 33 shrinkage (ppm) density (g/cm³) 2.38 2.40 2.40 2.50 2.55 2.38 2.41 2.42 strain point (° C.) 731 681 693 689 682 695 702 703 melting 1640 1554 1560 1548 1541 1614 1610 1608 temperature (° C.) liquidus viscosity 4.9 4.7 4.6 4.3 4.4 5.1 5.0 5.1 (log η) specific resistance 207 179 191 108 73 193 196 197 (Ω · cm) (1550° C.) etching rate (μm/h) 64 83 85 81 92 69 69 69 Comparative Examples 2-1 2-2 2-3 2-4 2-5 2-6 Compo- SiO₂ 71.7 71.7 66.4 67.64 67.64 67.64 sition B₂O₃ 4.0 11.0 7.83 7.83 7.83 (mol %) Al₂O₃ 11.1 11.1 10.9 12.73 12.73 12.73 K₂O 0.18 0.17 0.17 0.17 MgO 2.8 1 3 5 CaO 13.1 17.1 6.8 10.5 8.5 6.5 SrO 1.69 BaO SnO₂ 0.08 0.09 0.09 0.08 0.08 0.08 Fe₂O₃ 0.03 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 20.7 7.0 10.3 10.3 10.3 B₂O₃ SiO₂ + Al₂O₃ 82.8 82.8 77.4 80.4 80.4 80.4 RO + B₂O₃ + 17.1 17.1 22.3 19.4 19.4 19.4 ZnO Al₂O₃/SiO₂ 0.15 0.15 0.16 0.19 0.19 0.19 RO 13.1 17.1 11.3 11.5 11.5 11.5 B₂O₃ + P₂O₅ 4.0 11.0 7.83 7.83 7.83 CaO/RO 1 1 0.60 0.91 0.74 0.57 SiO₂—Al₂O₃/2 66.1 66.1 61.0 61.3 61.3 61.3 β-OH 0.13 0.11 0.11 0.11 0.11 0.12 Properties devitrification 1282 1330 1196 1260 1294 1324 temperature (° C.) Tg (° C.) 786 826 707 758 749 746 average coeffi- 29.8 41.0 34.3 34.4 33.3 32.8 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 17 13 114 32 37 38 shrinkage (ppm) density (g/cm³) 2.445 2.510 2.40 2.41 2.40 2.40 strain point (° C.) 725 774 660 708 697 691 melting 1675 1701 1529 1585 1580 1577 temperature (° C.) liquidus viscosity 4.7 4.4 4.6 4.4 4.2 4.0 (log η) specific resistance 230 188 165 132 130 128 (Ω · cm) (1550° C.) etching rate (μm/h) 65 65 82 83 81 79

<Third Glass Substrate>

The third glass substrate will be described by way of example. Note that the third glass substrate includes a glass comprising, as expressed in mol %,

65-78% SiO₂

3-20% Al₂O₃

3-15% B₂O₃

0% to less than 2% MgO

3.6-16% CaO

0-2% SrO

0% to less than 1% BaO

where

the contents in mol % of B₂O₃, P₂O₅, and CaO satisfy relationships B₂O₃+P₂O₅=3-15% and CaO/B₂O₃>1.2,

the strain point of the glass is 665° C. or more, and

the devitrification temperature of the glass is 1250° C. or less.

Examples and comparative examples of the sample glass having glass compositions shown in Table 3 were produced in a manner similar to that of the examples and comparative examples of the first glass substrate, and the properties thereof were measured.

TABLE 3 Examples 3-1 3-2 3-3 3-4 3-5 3-6 3-7 3-8 3-9 3-10 3-11 Compo- SiO₂ 71.7 71.6 70.8 70.5 70.5 70.3 67.5 67.3 67.8 66.9 72.0 sition B₂O₃ 6.0 6.0 6.9 7.4 7.4 7.8 7.5 8.3 7.8 9.2 6.4 (mol %) Al₂O₃ 11.1 11.1 11.0 10.9 10.9 10.9 12.9 12.7 12.5 12.2 11.4 K₂O 0.17 0.17 0.17 0.17 0.20 0.17 0.17 0.17 0.17 MgO 1.0 CaO 11.1 11.1 11.0 10.9 9.9 10.9 11.7 11.5 11.5 11.4 9.9 SrO BaO SnO₂ 0.08 0.08 0.08 0.08 0.08 0.08 0.10 0.08 0.08 0.08 0.08 Fe₂O₃ 0.022 0.022 0.022 0.022 0.02 0.02 0.02 0.02 0.022 (SiO₂ + Al₂O₃)/ 13.8 13.8 11.8 11.0 11.0 10.3 10.7 9.7 10.3 8.6 13.1 B₂O₃ SiO₂ + Al₂O₃ 82.8 82.6 81.8 81.4 81.4 81.2 80.4 80.0 80.4 79.2 83.4 RO + B₂O₃ + 17.1 17.1 17.9 18.3 18.3 18.7 19.2 19.8 19.4 20.5 16.3 ZnO Al₂O₃/SiO₂ 0.15 0.15 0.15 0.15 0.15 0.15 0.19 0.19 0.18 0.18 0.16 RO 11.1 11.1 11.0 10.9 10.9 10.9 11.7 11.5 11.5 11.4 9.9 B₂O₃ + P₂O₅ 6.0 6.0 6.9 7.4 7.4 7.8 7.5 8.3 7.8 9.2 6.4 CaO/RO 1 1 1 1 0.91 1 1 1 1 1 1 SiO₂—Al₂O₃/2 66.1 66.0 65.4 65.0 65.0 64.8 61.1 61.0 61.6 60.8 66.3 β-OH 0.11 0.12 0.11 0.11 0.12 0.13 0.12 0.11 0.11 0.10 0.12 Properties devitrification 1233 1230 1213 1189 1206 1187 1230 1220 1236 1193 1235 temperature (° C.) Tg (° C.) 782 776 766 758 751 761 763 754 760 741 781 average coeffi- 34.2 34.0 32.9 32.6 33.1 33.2 36.0 35.9 36.0 36.1 33.3 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 31 36 44 48 52 46 28 33 31 40 23 shrinkage (ppm) density (g/cm³) 2.41 2.41 2.40 2.39 2.39 2.38 2.40 2.41 2.42 2.40 2.38 strain point (° C.) 723 716 707 709 704 707 712 702 710 695 731 melting 1644 1632 1620 1608 1609 1610 1587 1582 1579 1567 1640 temperature (° C.) liquidus viscosity 5.0 5.0 5.1 5.2 5.0 5.2 4.6 4.7 4.6 4.9 4.9 (log η) specific resistance 243 193 194 195 194 248 137 133 129 142 207 (Ω · cm) (1550° C.) etching rate (μm/h) 65 65 67 69 69 69 80 82 80 83 64 Examples Comparative Examples 3-12 3-13 3-14 3-1 3-2 3-3 3-4 3-5 3-6 Compo- SiO₂ 66.5 70.5 70.5 71.7 71.7 66.4 67.64 67.64 67.64 sition B₂O₃ 9.5 7.4 7.4 4.0 11.0 7.83 7.83 7.83 (mol %) Al₂O₃ 11.4 10.9 10.9 11.1 11.1 10.9 12.73 12.73 12.73 K₂O 0.17 0.17 0.17 0.18 0.17 0.17 0.17 MgO 2.8 1 3 5 CaO 12.3 9.9 8.9 13.1 17.1 6.8 10.5 8.5 6.5 SrO 1.0 2.0 1.69 BaO SnO₂ 0.08 0.08 0.08 0.08 0.09 0.09 0.08 0.08 0.08 Fe₂O₃ 0.022 0.022 0.022 0.03 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 8.2 11.0 11.0 20.7 7.0 10.3 10.3 10.3 B₂O₃ SiO₂ + Al₂O₃ 77.9 81.4 81.4 82.8 82.8 77.4 80.4 80.4 80.4 RO + B₂O₃ + 21.8 18.3 18.3 17.1 17.1 22.3 19.4 19.4 19.4 ZnO Al₂O₃/SiO₂ 0.17 0.15 0.15 0.15 0.15 0.16 0.19 0.19 0.19 RO 12.3 10.9 10.9 13.1 17.1 11.3 11.5 11.5 11.5 B₂O₃ + P₂O₅ 9.5 7.4 7.4 4.0 11.0 7.83 7.83 7.83 CaO/RO 1 0.91 0.82 1 1 0.60 0.91 0.74 0.57 SiO₂—Al₂O₃/2 60.7 65.0 65.0 66.1 66.1 61.0 61.3 61.3 61.3 β-OH 0.11 0.12 0.12 0.13 0.11 0.11 0.11 0.11 0.12 Properties devitrification 1196 1207 1200 1282 1330 1196 1260 1294 1324 temperature (° C.) Tg (° C.) 731 752 753 786 826 707 758 749 746 average coeffi- 37.2 35.0 35.8 29.8 41.0 34.3 34.4 33.3 32.8 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 47 34 33 17 13 114 32 37 38 shrinkage (ppm) density (g/cm³) 2.40 2.41 2.42 2.445 2.510 2.40 2.41 2.40 2.40 strain point (° C.) 681 702 703 725 774 660 708 697 691 melting 1554 1610 1608 1675 1701 1529 1585 1580 1577 temperature (° C.) liquidus viscosity 4.7 5.0 5.1 4.7 4.4 4.6 4.4 4.2 4.0 (log η) specific resistance 179 196 197 230 188 165 132 130 128 (Ω · cm) (1550° C.) etching rate (μm/h) 83 69 69 65 65 82 83 81 79

<Fourth Glass Substrate>

The fourth glass substrate will be described by way of example. Note that the fourth glass substrate includes a glass comprising, as expressed in mol %,

65-78% SiO₂

3-20% Al₂O₃

3-9.5% B₂O₃

0% to less than 2% MgO

3.6-16% CaO

0-2% SrO

substantially no BaO

where

the contents in mol % of B₂O₃, P₂O₅, and CaO satisfy relationships B₂O₃+P₂O₅=3-9.5% and CaO/B₂O₃>1.2, and the devitrification temperature of the glass is 1250° C. or less.

Examples and comparative examples of the sample glass having glass compositions shown in Table 4 were produced in a manner similar to that of the examples and comparative examples of the first glass substrate, and the properties thereof were measured.

TABLE 4 Examples 4-1 4-2 4-3 4-4 4-5 4-6 4-7 4-8 4-9 4-10 Compo- SiO₂ 71.7 71.6 70.8 70.5 70.5 70.3 67.5 67.3 67.8 66.9 sition B₂O₃ 6.0 6.0 6.9 7.4 7.4 7.8 7.5 8.3 7.8 9.2 (mol %) Al₂O₃ 11.1 11.1 11.0 10.9 10.9 10.9 12.9 12.7 12.5 12.2 K₂O 0.17 0.17 0.17 0.17 0.20 0.17 0.17 0.17 MgO 1.0 CaO 11.1 11.1 11.0 10.9 9.9 10.9 11.7 11.5 11.5 11.4 SrO BaO SnO₂ 0.08 0.08 0.08 0.08 0.08 0.08 0.10 0.08 0.08 0.08 Fe₂O₃ 0.022 0.022 0.022 0.022 0.02 0.02 0.02 0.02 (SiO₂ + Al₂O₃)/ 13.8 13.8 11.8 11.0 11.0 10.3 10.7 9.7 10.3 8.6 B₂O₃ SiO₂ + Al₂O₃ 82.8 82.6 81.8 81.4 81.4 81.2 80.4 80.0 80.4 79.2 RO + B₂O₃ + 17.1 17.1 17.9 18.3 18.3 18.7 19.2 19.8 19.4 20.5 ZnO Al₂O₃/SiO₂ 0.15 0.15 0.15 0.15 0.15 0.15 0.19 0.19 0.18 0.18 RO 11.1 11.1 11.0 10.9 10.9 10.9 11.7 11.5 11.5 11.4 B₂O₃ + P₂O₅ 6.0 6.0 6.9 7.4 7.4 7.8 7.5 8.3 7.8 9.2 CaO/RO 1 1 1 1 0.91 1 1 1 1 1 SiO₂—Al₂O₃/2 66.1 66.0 65.4 65.0 65.0 64.8 61.1 61.0 61.6 60.8 β-OH 0.11 0.12 0.11 0.11 0.12 0.13 0.12 0.11 0.11 0.10 Properties devitrification 1233 1230 1213 1189 1206 1187 1230 1220 1236 1193 temperature (° C.) Tg (° C.) 782 776 766 758 751 761 763 754 760 741 average coeffi- 34.2 34.0 32.9 32.6 33.1 33.2 36.0 35.9 36.0 36.1 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 31 36 44 48 52 46 28 33 31 40 shrinkage (ppm) density (g/cm³) 2.41 2.41 2.40 2.39 2.39 2.38 2.40 2.41 2.42 2.40 strain point (° C.) 723 716 707 709 704 707 712 702 710 695 melting 1644 1632 1620 1608 1609 1610 1587 1582 1579 1567 temperature (° C.) liquidus viscosity 5.0 5.0 5.1 5.2 5.0 5.2 4.6 4.7 4.6 4.9 (log η) specific resistance 243 193 194 195 194 248 137 133 129 142 (Ω · cm) (1550° C.) etching rate (μm/h) 65 65 67 69 69 69 80 82 80 83 Examples Comparative Examples 4-11 4-12 4-13 4-1 4-2 4-3 4-4 4-5 4-6 Compo- SiO₂ 72.0 70.5 70.5 71.7 71.7 66.4 67.64 67.64 67.64 sition B₂O₃ 6.4 7.4 7.4 4.0 11.0 7.83 7.83 7.83 (mol %) Al₂O₃ 11.4 10.9 10.9 11.1 11.1 10.9 12.73 12.73 12.73 K₂O 0.17 0.17 0.17 0.18 0.17 0.17 0.17 MgO 2.8 1 3 5 CaO 9.9 9.9 8.9 13.1 17.1 6.8 10.5 8.5 6.5 SrO 1.0 2.0 1.69 BaO SnO₂ 0.08 0.08 0.08 0.08 0.09 0.09 0.08 0.08 0.08 Fe₂O₃ 0.022 0.022 0.022 0.03 0.022 0.022 0.022 (SiO₂ + Al₂O₃)/ 13.1 11.0 11.0 20.7 7.0 10.3 10.3 10.3 B₂O₃ SiO₂ + Al₂O₃ 83.4 81.4 81.4 82.8 82.8 77.4 80.4 80.4 80.4 RO + B₂O₃ + 16.3 18.3 18.3 17.1 17.1 22.3 19.4 19.4 19.4 ZnO Al₂O₃/SiO₂ 0.16 0.15 0.15 0.15 0.15 0.16 0.19 0.19 0.19 RO 9.9 10.9 10.9 13.1 17.1 11.3 11.5 11.5 11.5 B₂O₃ + P₂O₅ 6.4 7.4 7.4 4.0 11.0 7.83 7.83 7.83 CaO/RO 1 0.91 0.82 1 1 0.60 0.91 0.74 0.57 SiO₂—Al₂O₃/2 66.3 65.0 65.0 66.1 66.1 61.0 61.3 61.3 61.3 β-OH 0.12 0.12 0.12 0.13 0.11 0.11 0.11 0.11 0.12 Properties devitrification 1235 1207 1200 1282 1330 1196 1260 1294 1324 temperature (° C.) Tg (° C.) 781 752 753 786 826 707 758 749 746 average coeffi- 33.3 35.0 35.8 29.8 41.0 34.3 34.4 33.3 32.8 cient of thermal expansion (×10⁻⁷) (100-300° C.) rate of heat 23 34 33 17 13 114 32 37 38 shrinkage (ppm) density (g/cm³) 2.38 2.41 2.42 2.445 2.510 2.40 2.41 2.40 2.40 strain point (° C.) 731 702 703 725 774 660 708 697 691 melting 1640 1610 1608 1675 1701 1529 1585 1580 1577 temperature (° C.) liquidus viscosity 4.9 5.0 5.1 4.7 4.4 4.6 4.4 4.2 4.0 (log η) specific resistance 207 196 197 230 188 165 132 130 128 (Ω · cm) (1550° C.) etching rate (μm/h) 64 69 69 65 65 82 83 81 79

The flat panel display glass substrate of the present invention is suitable for flat panel displays in which the p-Si is used, and is particularly suitable as a glass substrate for liquid crystal displays and organic EL displays in which the p-Si TFT is used. The flat panel display glass substrate of the present invention is suitable as a display glass substrate for mobile terminals for which a high resolution is required, among other things.

Note that the specific embodiments or examples described in the “DETAILED DESCRIPTION OF THE INVENTION” section are only for the purpose of illustrating the technical aspects of the present invention, and are not to be construed in a narrow sense by limiting the present invention to such specific examples. Various changes and modifications can be made without departing from the spirit and scope of the present invention as set forth in the following claims. 

What is claimed is:
 1. A flat panel display glass substrate on which a p-Si TFT can be formed, the flat panel display glass substrate comprising a glass comprising, as expressed in mol %: 55-80% SiO₂; 3-20% Al₂O₃; 3-15% B₂O₃; and 3-25% RO, where RO represents the total amount of MgO, CaO, SrO, and BaO, wherein in the glass, the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17, the strain point of the glass is 665° C. or more, the devitrification temperature of the glass is 1250° C. or less, the glass substrate has a rate of heat shrinkage of 75 ppm or less, and the rate of heat shrinkage is calculated from the amount of shrinkage of the glass substrate measured after a heat treatment which is performed at a rising and falling temperature rate of 10° C./min and at 550° C. for 2 hours by; the rate of heat shrinkage (ppm)={the amount of shrinkage of the glass substrate after the heat treatment/the length of the glass substrate before the heat treatment}×10⁶.
 2. A flat panel display glass substrate on which a p-Si TFT can be formed, the flat panel display glass substrate comprising a glass comprising, as expressed in mol %; 55-80% SiO₂; 3-20% Al₂O₃; 3-15% B₂O₃; and 3-25% RO, where RO represents the total amount of MgO, CaO, SrO, and BaO, wherein in the glass the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0, the devitrification temperature of the glass is 1250° C. or less, the glass substrate has a rate of heat shrinkage of 60 ppm or less, and the rate of heat shrinkage is calculated from the amount of shrinkage of the glass substrate measured after a heat treatment which is performed at a rising and falling temperature rate of 10° C./min and at 550° C. for 2 hours by: the rate of heat shrinkage (ppm)={the amount of shrinkage of the glass substrate after the heat treatment/the length of the glass substrate before the heat treatment}×10⁶.
 3. The flat panel display glass substrate according to claim 1, wherein the glass contains, as expressed in mol %, 0-5% ZnO, in the glass, the contents in mol % of SiO₂ and Al₂O₃ satisfy SiO₂+Al₂O₃≧75%, and the contents in mol % of RO, ZnO, and B₂O₃ satisfy RO+ZnO+B₂O₃=7-25%.
 4. The flat panel display glass substrate according to claim 2, wherein the glass comprises, as expressed in mol %, 0-5% ZnO, in the glass, the contents in mol % of SiO₂ and Al₂O₃ satisfy SiO₂+Al₂O₃≧75%, and the contents in mol % of RO, ZnO, and B₂O₃ satisfy RO+ZnO+B₂O₃=7-25%.
 5. The flat panel display glass substrate according to claim 1, wherein in the glass, the sum of the MgO, CaO, SrO, and BaO contents is 4-20 mol %.
 6. The flat panel display glass substrate according to claim 2, wherein in the glass, the sum of the MgO, CaO, SrO, and BaO contents is 4-20 mol %.
 7. The flat panel display glass substrate according to claim 1, wherein in the glass, the ratio of the CaO content to the sum of the MgO, CaO, SrO, and BaO contents in mol % is more than 0.5.
 8. The flat panel display glass substrate according to claim 2, wherein in the glass, the ratio of the CaO content to the sum of the MgO, CaO, SrO, and BaO contents in mol % is more than 0.5.
 9. The flat panel display glass substrate according to claim 1, wherein the liquidus viscosity of the glass is 10^(4.5) dPa·s or more, and the flat panel display glass substrate is obtained by forming the glass using a downdraw process.
 10. The flat panel display glass substrate according to claim 2, wherein the liquidus viscosity of the glass is 10^(4.5) dPa·s or more, and the flat panel display glass substrate is obtained by forming the glass using a downdraw process.
 11. The flat panel display glass substrate according to claim 1, wherein the glass comprises substantially no As₂O₃ or Sb₂O₃.
 12. The flat panel display glass substrate according to claim 2, wherein the glass comprises substantially no As₂O₃ or Sb₂O₃.
 13. The flat panel display glass substrate according to claim 1, wherein the flat panel display glass substrate is a liquid crystal display glass substrate.
 14. The flat panel display glass substrate according to claim 2, wherein the flat panel display glass substrate is a liquid crystal display glass substrate.
 15. A flat panel display glass substrate comprising a glass comprising, as expressed in mol %: 55-80% SiO₂; 3-20% Al₂O₃; 3-15% B₂O₃; and 3-25% RO, where RO represents the total amount of MgO, CaO, SrO, and BaO, wherein in the glass, the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17, the strain point of the glass is 665° C. or more, the devitrification temperature of the glass is 1250° C. or less, the glass substrate has a rate of heat shrinkage of 75 ppm or less, and the rate of heat shrinkage is calculated from the amount of shrinkage of the glass substrate measured after a heat treatment which is performed at a rising and falling temperature rate of 10° C./min and at 550° C. for 2 hours by: the rate of heat shrinkage (ppm)={the amount of shrinkage of the glass substrate after the heat treatment/the length of the glass substrate before the heat treatment}×10⁶.
 16. A flat panel display glass substrate comprising a glass comprising, as expressed in mol %: 55-80% SiO₂; 3-20% Al₂O₃; 3-15% B₂O₃; and 3-25% RO, where RO represents the total amount of MgO, CaO, SrO, and BaO, wherein in the glass, the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=8.45-17.0, the devitrification temperature of the glass is 1250° C. or less, the glass substrate has a rate of heat shrinkage of 60 ppm or less, and the rate of heat shrinkage is calculated from the amount of shrinkage of the glass substrate measured after a heat treatment which is performed at a rising and falling temperature rate of 10° C./min and at 550° C. for 2 hours by: the rate of heat shrinkage (ppm)={the amount of shrinkage of the glass substrate after the heat treatment/the length of the glass substrate before the heat treatment}×10⁶.
 17. A flat panel display glass substrate on which a p-Si TFT can be formed, the flat panel display glass substrate comprising a glass comprising, as expressed in mol %: 55-80% SiO₂; 3-20% Al₂O₃; 3-15% B₂O₃; and 3-25% RO, where RO represents the total amount of MgO, CaO, SrO, and BaO, wherein in the glass, the contents in mol % of SiO₂, Al₂O₃, and B₂O₃ satisfy a relationship (SiO₂+Al₂O₃)/(B₂O₃)=7.5-17, the strain point of the glass is 665° C. or more, the devitrification temperature of the glass is 1250° C. or less, and the glass substrate has a rate of heat shrinkage of 75 ppm or less after a heat treatment in which the glass substrate is kept at Tg for 30 min, then cooled at a rate of 100° C./min until the temperature thereof reaches Tg−100° C., then cooled until the temperature reaches room temperature, and then kept at 550° C. for 2 hours, wherein a rising and falling temperature rate is 10° C./min. 